Research paper

Formation Mechanisms of Hot Cracks in Laser Additive Repairing Single Crystal Superalloys

  • LU Nannan ,
  • GUO Yimo ,
  • YANG Shulin ,
  • LIANG Jingjing ,
  • ZHOU Yizhou ,
  • SUN Xiaofeng ,
  • LI Jinguo
Expand
  • 1Shi -changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China
    2School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China
    3AECC Shenyang Liming Aero-Engine Co., Ltd., Shenyang 110043, China

Received date: 2023-04-03

  Revised date: 2023-05-09

  Online published: 2023-07-04

Supported by

National Key Research and Development Program of China(2021YFB3702503);China Postdoctoral Science Foundation(2022M723211)

Abstract

Hot cracking is a prevalent defect in metallurgy that often occurs during the laser additive repair of single crystal superalloys. The understanding of the cracking mechanism is vital for defect prevention. Consequently, this study entails combining experimental analysis and theoretical calculations to investigate the hot cracking mechanism in a second-generation single crystal superalloy, DD432, during laser additive repairing. The incident of hot cracking was observed predominantly at high-angle grain boundaries (HAGBs). High-magnitude stress concentrations were identified on both sides of the crack, accompanied by an extensive distribution of MC-type carbides in the crack initiation region. Hot cracking depended on factors such as liquid film stability, stress concentration, and MC-type carbide precipitates. The stability of the liquid film depended on dendrite coalescence undercooling, which in turn was related to the angle of grain boundaries. According to Rappaz's theory of dendrite coalescence undercooling, the calculated dendrite coalescence undercooling at HAGBs was 395 K. This figure was substantially higher than the 38 K liquid film undercooling found within a single dendrite, and far exceeded the undercooling at a low-angle grain boundary (3.6°) with a value of 56 K. The elevated level of stress concentration served as a driving force for crack initiation and propagation. MC-type carbide precipitates promoted crack initiation through a pinning effect on the liquid feed, thereby weakening the interface bonding strength with the substrate.

Cite this article

LU Nannan , GUO Yimo , YANG Shulin , LIANG Jingjing , ZHOU Yizhou , SUN Xiaofeng , LI Jinguo . Formation Mechanisms of Hot Cracks in Laser Additive Repairing Single Crystal Superalloys[J]. Acta Metall Sin, 2023 , 59(9) : 1243 -1252 . DOI: 10.11900/0412.1961.2023.00147

References

1 Reed R C, Tao T, Warnken N. Alloys-by-design: Application to nickel-based single crystal superalloys [J]. Acta Mater., 2009, 57: 5898
2 Lopez-Galilea I, Ruttert B, He J Y, et al. Additive manufacturing of CMSX-4 Ni-base superalloy by selective laser melting: Influence of processing parameters and heat treatment [J]. Addit. Manuf., 2019, 30: 100874
3 Pollock T M. Alloy design for aircraft engines [J]. Nat. Mater., 2016, 15: 809
4 Wang L, Wang N, Yao W J, et al. Effect of substrate orientation on the columnar-to-equiaxed transition in laser surface remelted single crystal superalloys [J]. Acta Mater., 2015, 88: 283
5 Liang Y J, Cheng X, Li J, et al. Microstructural control during laser additive manufacturing of single-crystal nickel-base superalloys: New processing-microstructure maps involving powder feeding [J]. Mater. Des., 2017, 130: 197
6 Ur Rahman N, Capuano L, Cabeza S, et al. Directed energy deposition and characterization of high-carbon high speed steels [J]. Addit. Manuf., 2019, 30: 100838
7 Zhou Z P, Huang L, Shang Y J, et al. Causes analysis on cracks in nickel-based single crystal superalloy fabricated by laser powder deposition additive manufacturing [J]. Mater. Des., 2018, 160: 1238
8 Thompson S M, Bian L K, Shamsaei N, et al. An overview of direct laser deposition for additive manufacturing; Part I: Transport phenomena, modeling and diagnostics [J]. Addit. Manuf., 2015, 8: 36
9 G?umann M, Bezen?on C, Canalis P, et al. Single-crystal laser deposition of superalloys: Processing-microstructure maps [J]. Acta Mater., 2001, 49: 1051
10 Liang Y J, Wang H M. Origin of stray-grain formation and epitaxy loss at substrate during laser surface remelting of single-crystal nickel-base superalloys [J]. Mater. Des., 2016, 102: 297
11 Wang L, Wang N. Effect of substrate orientation on the formation of equiaxed stray grains in laser surface remelted single crystal superalloys: Experimental investigation [J]. Acta Mater., 2016, 104: 250
12 Guo J C, Chen W J, Yang R N, et al. The effect of substrate orientation on stray grain formation in the (111) plane in laser surface remelted single crystal superalloys [J]. J. Alloys Compd., 2019, 800: 240
13 Wang L, Wang N, Provatas N. Liquid channel segregation and morphology and their relation with hot cracking susceptibility during columnar growth in binary alloys [J]. Acta Mater., 2017, 126: 302
14 Wang N, Mokadem S, Rappaz M, et al. Solidification cracking of superalloy single- and bi-crystals [J]. Acta Mater., 2004, 52: 3173
15 Carter L N, Martin C, Withers P J, et al. The influence of the laser scan strategy on grain structure and cracking behaviour in SLM powder-bed fabricated nickel superalloy [J]. J. Alloys Compd., 2014, 615: 338
16 Ruttert B, Ramsperger M, Roncery L M, et al. Impact of hot isostatic pressing on microstructures of CMSX-4 Ni-base superalloy fabricated by selective electron beam melting [J]. Mater. Des., 2016, 110: 720
17 Ojo O A, Richards N L, Chaturvedi M C. Contribution of constitutional liquation of gamma prime precipitate to weld HAZ cracking of cast Inconel 738 superalloy [J]. Scr. Mater., 2004, 50: 641
18 Chauvet E, Kontis P, J?gle E A, et al. Hot cracking mechanism affecting a non-weldable Ni-based superalloy produced by selective electron Beam Melting [J]. Acta Mater., 2018, 142: 82
19 Ramakrishnan A, Dinda G P. Direct laser metal deposition of Inconel 738 [J]. Mater. Sci. Eng., 2019, A740-741: 1
20 Boswell J H, Clark D, Li W, et al. Cracking during thermal post-processing of laser powder bed fabricated CM247LC Ni-superalloy [J]. Mater. Des., 2019, 174: 107793
21 Yang J J, Li F Z, Wang Z M, et al. Cracking behavior and control of Rene 104 superalloy produced by direct laser fabrication [J]. J. Mater. Process. Technol., 2015, 225: 229
22 Dantzig J A, Rappaz M. Solidification [M]. 2nd Edition -Revised & Expanded. Switzerland: EPFL Press, 2016: 618
23 Rong P, Wang N, Wang L, et al. The influence of grain boundary angle on the hot cracking of single crystal superalloy DD6 [J]. J. Alloys Compd., 2016, 676: 181
24 Ci S W. Study on microstructure and mechanical properties of nickel-based single crystal superalloy by laser additive manufacturing [D]. Shenyang: University of Science and Technology of China(Institute of Metal Research, CAS), 2021
  慈世伟. 激光增材制造镍基单晶高温合金显微组织和力学性能研究 [D]. 沈阳: 中国科学技术大学(中国科学院金属研究所), 2021
25 Lu N N, Lei Z L, Hu K, et al. Hot cracking behavior and mechanism of a third-generation Ni-based single-crystal superalloy during directed energy deposition [J]. Addit. Manuf., 2020, 34: 101228
26 Rappaz M, Drezet J M, Gremaud M. A new hot-tearing criterion [J]. Metall. Mater. Trans., 1999, 30A: 449
27 Rappaz M, Jacot A, Boettinger W J. Last-stage solidification of alloys: Theoretical model of dendrite-arm and grain coalescence [J]. Metall. Mater. Trans., 2003, 34A: 467
28 Anderson P M, Hirth J P, Lothe J. Theory of Dislocations [M]. 3rd Ed., Cambridge: Cambridge University Press, 2017: 536
29 Academic Committee of the Superalloys. China Superalloys Handbook [M]. Beijing: Standards Press of China, 2012: 589
  中国金属学会高温材料分会. 中国高温合金手册 [M]. 北京: 中国标准出版社, 2012: 589
30 Read W T, Shockley W. Dislocation models of crystal grain boundaries [J]. Phys. Rev., 1950, 78: 275
31 Asta M, Hoyt J J, Karma A. Calculation of alloy solid-liquid interfacial free energies from atomic-scale simulations [J]. Phys. Rev., 2002, 66B: 100101
32 Kurz W, Fisher D J. Fundamentals of Solidification [M]. 4th Ed., Switzerland: Trans Tech Publications Ltd, 1998: 51
33 Debroy T, Wei H L, Zuback J S, et al. Additive manufacturing of metallic components—Process, structure and properties [J]. Prog. Mater. Sci., 2018, 92: 112
34 Frenk A, Marsden C F, Wagniere J D, et al. Influence of an intermediate layer on the residual stress field in a laser clad [J]. Surf. Coat. Technol., 1991, 45: 435
35 Mukherjee T, Zhang W, Debroy T. An improved prediction of residual stresses and distortion in additive manufacturing [J]. Comput. Mater. Sci., 2017, 126: 360
36 Kattamis T Z, Voorhees P W. Coarsening of solid-liquid mixtures: A review [A]. Proceedings of the Merton C. Flemings Symposium on Solidification and Materials Processing [C]. Cambridge, MA: TMS, 2000: 119
37 Huang Q Y, Li H K. Superalloys [M]. Beijing: Metallurgical Industry Press, 2000: 67
  黄乾尧, 李汉康. 高温合金 [M]. 北京: 冶金工业出版社, 2000: 67
Outlines

/