Mechanism of Grain Refinement of Pulse Current Assisted Plasma Arc Welded Al-Mg Alloy
Received date: 2022-01-25
Revised date: 2022-03-14
Online published: 2022-08-29
Supported by
National Natural Science Foundation of China(51704013);Beijing Municipal Education Commission Fund(KM201810005016);Technology Fund of Beijing University of Technology(ykj-2018-00325)
During welding, the vibration effect of applying a pulse current on the molten pool can effectively improve weld formation and refine grains. The effect of pulse current on grain refinement and its mechanism were studied for Al-Mg alloy welds fabricated by conventional plasma welding (PAW), PAW with conventional pulse current, and PAW with composite pulse current. The grain size produced by conventional PAW was 78.2 μm, whereas the average grain size was reduced from 78.2 μm to 53.3 μm with increasing conventional pulse current frequency from 0 Hz to 100 Hz; in addition, the degree of grain refinement increased by about 30%. However, the minimum grain size was 48.2 μm, and the grain refinement effect can reach nearly 40% by combining low-frequency pulse current with conventional pulse current. The proportion of small grains and high-angle grain boundaries increased significantly after applying the composite pulse current. The additional oscillation effect of the composite pulse current can effectively eliminate coarse grains during the solidification of the weld pool. The main mechanism of grain refinement is dendrite fragmentation, which is discussed through thermodynamics and composition.
Key words： PAW; Al-Mg alloy; composite pulse current; grain refinement; dendrite fragmentation
YUAN Tao , ZHAO Xiaohu , JIANG Xiaoqing , REN Xuelei , LI Boyang . Mechanism of Grain Refinement of Pulse Current Assisted Plasma Arc Welded Al-Mg Alloy[J]. Acta Metall Sin, 2024 , 60(3) : 323 -332 . DOI: 10.11900/0412.1961.2022.00036
| 1 | Kruth J P, Levy G, Klocke F, et al. Consolidation phenomena in laser and powder-bed based layered manufacturing [J]. CIRP Annals, 2007, 56: 730 |
| 2 | Santos M C, Machado A R, Sales W F, et al. Machining of aluminum alloys: A review [J]. Int. J. Adv. Manuf. Technol., 2016, 86: 3067 |
| 3 | Spierings A B, Dawson K, Heeling T, et al. Microstructural features of Sc- and Zr-modified Al-Mg alloys processed by selective laser melting [J]. Mater. Des., 2017, 115: 52 |
| 4 | Croteau J R, Griffiths S, Rossell M D, et al. Microstructure and mechanical properties of Al-Mg-Zr alloys processed by selective laser melting [J]. Acta Mater., 2018, 153: 35 |
| 5 | Chakrabarti D J, Laughlin D E. Phase relations and precipitation in Al-Mg-Si alloys with Cu additions [J]. Prog. Mater. Sci., 2004, 49: 389 |
| 6 | Zhang Z Q, He C S, Li Y, et al. Effects of ultrasonic assisted friction stir welding on flow behavior, microstructure and mechanical properties of 7N01-T4 aluminum alloy joints [J]. J. Mater. Sci. Technol., 2020, 43: 1 |
| 7 | Dai W L. Effects of high-intensity ultrasonic-wave emission on the weldability of aluminum alloy 7075-T6 [J]. Mater. Lett., 2003, 57: 2447 |
| 8 | Rao S R K, Reddy G M, Kamaraj M, et al. Grain refinement through arc manipulation techniques in Al-Cu alloy GTA welds [J]. Mater. Sci. Eng., 2005, A404: 227 |
| 9 | Babu N K, Talari M K, Pan D, et al. Microstructural characterization and grain refinement of AA6082 gas tungsten arc welds by scandium modified fillers [J]. Mater. Chem. Phys., 2012, 137: 543 |
| 10 | Liotti E, Lui A, Vincent R, et al. A synchrotron X-ray radiography study of dendrite fragmentation induced by a pulsed electromagnetic field in an Al-15Cu alloy [J]. Acta Mater., 2014, 70: 228 |
| 11 | Yuan T, Kou S, Luo Z. Grain refining by ultrasonic stirring of the weld pool [J]. Acta Mater., 2016, 106: 144 |
| 12 | Wang G, Dargusch M S, Qian M, et al. The role of ultrasonic treatment in refining the as-cast grain structure during the solidification of an Al-2Cu alloy [J]. J. Cryst. Growth, 2014, 408: 119 |
| 13 | Villaret V, Deschaux-Beaume F, Bordreuil C. A solidification model for the columnar to equiaxed transition in welding of a Cr-Mo ferritic stainless steel with Ti as inoculant [J]. J. Mater. Process. Technol., 2016, 233: 115 |
| 14 | Bermingham M J, McDonald S D, Dargusch M S, et al. The mechanism of grain refinement of titanium by silicon [J]. Scr. Mater., 2008, 58: 1050 |
| 15 | Samanta S K, Mitra S K, Pal T K. Effect of rare earth elements on microstructure and oxidation behaviour in TIG weldments of AISI 316L stainless steel [J]. Mater. Sci. Eng., 2006, A430: 242 |
| 16 | Chen Z N, Kang H J, Fan G H, et al. Grain refinement of hypoeutectic Al-Si alloys with B [J]. Acta Mater., 2016, 120: 168 |
| 17 | Song B, Dong S J, Coddet P, et al. Microstructure and tensile behavior of hybrid nano-micro SiC reinforced iron matrix composites produced by selective laser melting [J]. J. Alloys Compd., 2013, 579: 415 |
| 18 | AlMangour B, Grzesiak D, Yang J M. Selective laser melting of TiB2/H13 steel nanocomposites: influence of hot isostatic pressing post-treatment [J]. J. Mater. Process. Technol., 2017, 244: 344 |
| 19 | Xi L X, Gu D D, Guo S, et al. Grain refinement in laser manufactured Al-based composites with TiB2 ceramic [J]. J. Mater. Res. Technol., 2020, 9: 2611 |
| 20 | Wang E Z, Gao T, Nie J F, et al. Grain refinement limit and mechanical properties of 6063 alloy inoculated by Al-Ti-C (B) master alloys [J]. J. Alloys Compd., 2014, 594: 7 |
| 21 | Easton M A, Schiffl A, Yao J, et al. Grain refinement of Mg-Al(-Mn) alloys by SiC additions [J]. Scr. Mater., 2006, 55: 379 |
| 22 | Kou S, Le Y. Grain structure and solidification cracking in oscillated arc welds of 5052 aluminum alloy [J]. Metall. Trans., 1985, 16A: 1345 |
| 23 | Yuan T, Luo Z, Kou S. Grain refining of magnesium welds by arc oscillation [J]. Acta Mater., 2016, 116: 166 |
| 24 | Jiang Z G, Chen X, Li H, et al. Grain refinement and laser energy distribution during laser oscillating welding of Invar alloy [J]. Mater. Des., 2020, 186: 108195 |
| 25 | Tseng K H, Chou C P. The effect of pulsed GTA welding on the residual stress of a stainless steel weldment [J]. J. Mater. Process. Technol., 2002, 123: 346 |
| 26 | Balasubramanian V, Ravisankar V, Reddy G M. Effect of pulsed current and post weld aging treatment on tensile properties of argon arc welded high strength aluminium alloy [J]. Mater. Sci. Eng., 2007, A459: 19 |
| 27 | Balasubramanian V, Ravisankar V, Madhusudhan Reddy G. Influences of pulsed current welding and post weld aging treatment on fatigue crack growth behaviour of AA7075 aluminium alloy joints [J]. Int. J. Fatigue, 2008, 30: 405 |
| 28 | Palani P K, Murugan N. Selection of parameters of pulsed current gas metal arc welding [J]. J. Mater. Process. Technol., 2006, 172: 1 |
| 29 | Liu A H, Tang X H, Lu F G. Study on welding process and prosperities of AA5754 Al-alloy welded by double pulsed gas metal arc welding [J]. Mater. Des., 2013, 50: 149 |
| 30 | Pan J J, Hu S S, Yang L J, et al. Investigation of molten pool behavior and weld bead formation in VP-GTAW by numerical modelling [J]. Mater. Des., 2016, 111: 600 |
| 31 | Wang Y P, Qi B J, Cong B Q, et al. Keyhole welding of AA2219 aluminum alloy with double-pulsed variable polarity gas tungsten arc welding [J]. J. Manuf. Process., 2018, 34: 179 |
| 32 | Wang Y P, Cong B Q, Qi B J, et al. Process characteristics and properties of AA2219 aluminum alloy welded by double pulsed VPTIG welding [J]. J. Mater. Process. Technol., 2019, 266: 255 |
| 33 | Bosworth M R, Deam R T. Influence of GMAW droplet size on fume formation rate [J]. J. Phys. D: Appl. Phys., 2000, 33: 2605 |
| 34 | Da Silva C L M, Scotti A. The influence of double pulse on porosity formation in aluminum GMAW [J]. J. Mater. Process. Technol., 2006, 171: 366 |
| 35 | Liu A H, Tang X H, Lu F G. Weld pool profile characteristics of Al alloy in double-pulsed GMAW [J]. Int. J. Adv. Manuf. Technol., 2013, 68: 2015 |
| 36 | Yao P, Zhou K, Tang H Q. Effects of operational parameters on the characteristics of ripples in double-pulsed GMAW process [J]. Materials, 2019, 12: 2767 |
| 37 | Wang L L, Wei H L, Xue J X, et al. A pathway to microstructural refinement through double pulsed gas metal arc welding [J]. Scr. Mater., 2017, 134: 61 |
| 38 | Wang Y P, Cong B Q, Qi B J, et al. Influence of low-pulsed frequency on arc profile and weld formation characteristics in double-pulsed VPTIG welding of aluminium alloys [J]. J. Manuf. Process., 2020, 58: 1211 |
| 39 | Wang L L, Xue J X. Perspective on double pulsed gas metal arc welding [J]. Appl. Sci., 2017, 7: 894 |
| 40 | Zhang P L, Jia Z Y, Yu Z S, et al. A review on the effect of laser pulse shaping on the microstructure and hot cracking behavior in the welding of alloys [J]. Opt. Laser Technol., 2021, 140: 107094 |
| 41 | Wang Y J, Chen M A, Wu C S. HF pulse effect on microstructure and properties of AC TIG butt-welded joint of 6061Al alloy [J]. J. Manuf. Process., 2020, 56: 878 |
| 42 | Wang Z M, Jiang D H, Wu J W, et al. A review on high-frequency pulsed arc welding [J]. J. Manuf. Processes, 2020, 60: 503 |
/
| 〈 |
|
〉 |