Electron Tomography Analysis on the Structure and Chemical Composition of Nanoporous Metal Surfaces
Received date: 2022-03-23
Revised date: 2022-05-17
Online published: 2022-05-30
Supported by
National Natural Science Foundation of China(52171020);National Natural Science Foundation of China(91960202)
Nanoporous metals have a porous structure with bicontinuous nanoscale voids and ligaments. Thus, nanoporous metals differ from their bulk counterparts in mechanical, physical, and chemical characteristics due to their unique ligament structure and high surface-to-volume ratio. The surface structure and chemistry of nanoporous metals play critical roles in their applications in catalysis, sensing, and other fields. The surfaces of nanoporous metals contain a substantial number of low-coordination sites, which are vital for improving their catalytic performance. Moreover, the addition of platinum to nanoporous gold has a massive impact on its catalytic and mechanical characteristics. High-resolution transmission electron microscopy (TEM) and high-resolution scanning transmission electron microscopy (STEM) are commonly used to study the atomic structure of crystals. However, since these techniques only provides two-dimensional projection images, it is usually hard or even impossible to directly and quantitatively resolve the three-dimensional (3D) structure of nanocrystals, especially their surface crystallography and coordination information. Compared to traditional TEM and STEM imaging technologies, electron tomography with atomic resolution provides a powerful means to resolve 3D atomic-resolution information of materials. In this work, the surface structure and chemical composition of nanoporous gold and nanoporous gold-platinum were analyzed using STEM, electron tomography, and three-dimensional reconstruction of energy dispersive spectroscopy (EDS) results. The atomic structure of the ligament surface was examined using electron tomography with atomic resolution. It was observed that, surface defects can be separated into two categories: kinks and steps on the {111} terrace, and dents and pits. Surface dents and pits introduce a greater number of low-coordination sites than kinks and steps. Furthermore, the segregation of Pt on the ligament surface was discovered by combining the atomic-resolution electron tomography with the 3D reconstruction of EDS results.
DUAN Huichao , WANG Chunyang , YE Hengqiang , DU Kui . Electron Tomography Analysis on the Structure and Chemical Composition of Nanoporous Metal Surfaces[J]. Acta Metall Sin, 2023 , 59(10) : 1291 -1298 . DOI: 10.11900/0412.1961.2022.00133
| 1 | Wittstock A, Wichmann A, Biener J, et al. Nanoporous gold: A new gold catalyst with tunable properties [J]. Faraday Discuss., 2011, 152: 87 |
| 2 | Zhang X M, Ding Y. Unsupported nanoporous gold for heterogeneous catalysis [J]. Catal. Sci. Technol., 2013, 3: 2862 |
| 3 | Jin H J, Wang X L, Parida S, et al. Nanoporous Au-Pt alloys as large strain electrochemical actuators [J]. Nano Lett., 2010, 10: 187 |
| 4 | Weissmuller J, Viswanath R N, Kramer D, et al. Charge-induced reversible strain in a metal [J]. Science, 2003, 300: 312 |
| 5 | Wittstock A, Biener J, B?umer M. Nanoporous gold: A new material for catalytic and sensor applications [J]. Phys. Chem. Chem. Phys., 2010, 12: 12919 |
| 6 | Huang J F, Sun I W. Fabrication and surface functionalization of nanoporous gold by electrochemical alloying/dealloying of Au-Zn in an ionic liquid, and the self‐assembly of L‐cysteine monolayers [J]. Adv. Funct. Mater., 2005, 15: 989 |
| 7 | Yu Y, Gu L, Lang X Y, et al. Li Storage in 3D nanoporous Au‐supported nanocrystalline tin [J]. Adv. Mater., 2011, 23: 2443 |
| 8 | Erlebacher J, Aziz M J, Karma A, et al. Evolution of nanoporosity in dealloying [J]. Nature, 2001, 410: 450 |
| 9 | Pickering H W. Characteristic features of alloy polarization curves [J]. Corros. Sci., 1983, 23: 1107 |
| 10 | Gao P P, Zhu Z J, Ye X L, et al. Defects evolution in nanoporous Au (Pt) during dealloying [J]. Scr. Mater., 2016, 113: 68 |
| 11 | Ye X L, Jin H J. Corrosion‐induced strengthening: Development of high‐strength nanoporous metals [J]. Adv. Eng. Mater., 2016, 18: 1050 |
| 12 | Weissmüller J, Newman R C, Jin H J, et al. Nanoporous metals by alloy corrosion: Formation and mechanical properties [J]. MRS Bull., 2009, 34: 577 |
| 13 | Molares M E T, Balogh A G, Cornelius T W, et al. Fragmentation of nanowires driven by Rayleigh instability [J]. Appl. Phys. Lett., 2004, 85: 5337 |
| 14 | Qian L H, Chen M W. Ultrafine nanoporous gold by low-temperature dealloying and kinetics of nanopore formation [J]. Appl. Phys. Lett., 2007, 91: 083105 |
| 15 | Jin H J, Parida S, Kramer D, et al. Sign-inverted surface stress-charge response in nanoporous gold [J]. Surf. Sci., 2008, 602: 3588 |
| 16 | Newman R C. A theory of secondary alloying effects on corrosion and stress-corrosion cracking [J]. Corros. Sci., 1992, 33: 1653 |
| 17 | Snyder J, Asanithi P, Dalton A B, et al. Stabilized nanoporous metals by dealloying ternary alloy precursors [J]. Adv. Mater., 2008, 20: 4883 |
| 18 | Erlebacher J. An atomistic description of dealloying: Porosity evolution, the critical potential, and rate-limiting behavior [J]. J. Electrochem. Soc., 2004, 151: C614 |
| 19 | Vega A A, Newman R C. Nanoporous metals fabricated through electrochemical dealloying of Ag-Au-Pt with systematic variation of Au: Pt ratio [J]. J. Electrochem. Soc., 2013, 161: C1 |
| 20 | Vega A A, Newman R C. Beneficial effects of adsorbate-induced surface segregation of Pt in nanoporous metals fabricated by dealloying of Ag-Au-Pt alloys [J]. J. Electrochem. Soc., 2014, 161: C11 |
| 21 | Vega A A, Newman R C. Methanol electro-oxidation on nanoporous metals formed by dealloying of Ag-Au-Pt alloys [J]. J. Appl. Electrochem., 2016, 46: 995 |
| 22 | El-Zoka A, Langelier B, Korinek A, et al. Nanoscale mechanism of the stabilization of nanoporous gold by alloyed platinum [J]. Nanoscale, 2018, 10: 4904 |
| 23 | Cai Y, Ma C, Zhu Y M, et al. Low-coordination sites in oxygen-reduction electrocatalysis: Their roles and methods for removal [J]. Langmuir, 2011, 27: 8540 |
| 24 | Barreau M, Méthivier C, Sturel T, et al. In situ surface imaging: high temperature environmental SEM study of the surface changes during heat treatment of an Al-Si coated boron steel [J]. Mater. Charact., 2020, 163: 110266 |
| 25 | Luo Y, Jelic V, Chen G, et al. Nanoscale terahertz STM imaging of a metal surface [J]. Phys. Rev., 2020, 102B: 205417 |
| 26 | Geagea E, Jeannoutot J, Féron M, et al. Collective radical oligomerisation induced by an STM tip on a silicon surface [J]. Nanoscale, 2021, 13: 349 |
| 27 | Li T, Kasian O, Cherevko S, et al. Atomic-scale insights into surface species of electrocatalysts in three dimensions [J]. Nat. Catal., 2018, 1: 300 |
| 28 | Nomoto K, Sugimoto H, Ceguerra A V, et al. 3D microstructure analysis of silicon-boron phosphide mixed nanocrystals [J]. Nanoscale, 2020, 12: 7256 |
| 29 | Yu R, Chen W, Cheng Z Y, et al. Multishell intermetallic onions by symmetrical configuration of ordered domains [J]. Phys. Rev. Lett., 2010, 105: 225501 |
| 30 | Yu R, Hu L H, Cheng Z Y, et al. Direct subangstrom measurement of surfaces of oxide particles [J]. Phys. Rev. Lett., 2010, 105: 226101 |
| 31 | He M R, Yu R, Zhu J. Reversible wurtzite-tetragonal reconstruction in ZnO (10 1 ˉ 0) surfaces [J]. Angew. Chem. Int. Ed., 2012, 51:7744 |
| 32 | Lu N, Du K, Lu L, et al. Transition of dislocation nucleation induced by local stress concentration in nanotwinned copper [J]. Nat. Commun., 2015, 6: 7648 |
| 33 | Wang C Y, Du K, Song K P, et al. Size-dependent grain-boundary structure with improved conductive and mechanical stabilities in sub-10-nm gold crystals [J]. Phys. Rev. Lett., 2018, 120: 186102 |
| 34 | Wang X L, Wang C Y, Chen C J, et al. Free-standing monatomic thick two-dimensional gold [J]. Nano Lett., 2019, 19: 4560 |
| 35 | Bals S, Casavola M, Van Huis M A, et al. Three-dimensional atomic imaging of colloidal core-shell nanocrystals [J]. Nano Lett., 2011, 11: 3420 |
| 36 | Scott M C, Chen C C, Mecklenburg M, et al. Electron tomography at 2.4-?ngstr?m resolution [J]. Nature, 2012, 483: 444 |
| 37 | Wang C Y, Duan H C, Chen C J, et al. Three-dimensional atomic structure of grain boundaries resolved by atomic-resolution electron tomography [J]. Matter, 2020, 3: 1999 |
| 38 | Wang C Y, Liu H Y, Duan H C, et al. 3D atomic imaging of low-coordinated active sites in solid-state dealloyed hierarchical nanoporous gold [J]. J. Mater. Chem., 2021, 9A: 25513 |
| 39 | Tran R, Xu Z H, Radhakrishnan B, et al. Surface energies of elemental crystals [J]. Sci. Data, 2016, 3: 160080 |
| 40 | Qi Z, Vainio U, Kornowski A, et al. Porous gold with a nested‐network architecture and ultrafine structure [J]. Adv. Funct. Mater., 2015, 25: 2530 |
| 41 | Ye X L, Lu N, Li X J, et al. Primary and secondary dealloying of Au(Pt)-Ag: Structural and compositional evolutions, and volume shrinkage [J]. J. Electrochem. Soc., 2014, 161: C517 |
/
| 〈 |
|
〉 |