Effects of Pre-Strain and Two-Step Aging on Microstructure and Mechanical Properties of Fe-30Mn-11Al-1.2C Austenitic Low-Density Steel
Received date: 2020-12-18
Revised date: 2021-05-06
Online published: 2021-05-28
Supported by
National Natural Science Foundation of China(51871062);National Natural Science Foundation of China(52171105);Fundamental Research Funds for the Central Universities(2020CDJDPT001)
Lightweight Fe-Mn-Al-C steels are promising candidates for automobile structural materials and have gained increased scientific and commercial interest owing to their outstanding mechanical properties and low density. To date, several studies have been conducted to illustrate the mechanism of phase transformation, strengthening, and strain hardening under solution and aging state. Moreover, prestrain before aging as a low-cost and simple method to tailor precipitates and control properties has been widely reported; however, it has been barely investigated in the Fe-Mn-Al-C alloy system. Therefore, in this study, the effects of pre-cold rolling and two-step aging on the microstructure and mechanical properties of Fe-30Mn-11Al-1.2C (mass fraction, %) austenitic low-density steel are investigated using EBSD, TEM, and universal testing machine. Results showed that the yield strength (YS) significantly increased via the two-step aging from 580 MPa (at solution state) to 1120 MPa, but the uniform elongation (UE) sharply decreased to approximately 0. However, after the pre-cold rolling and two-step aging, the YS of the material further improved to 1220 MPa, and the UE significantly increased to 18.2%, which implies an improvement in the comprehensive mechanical properties of the material. According to the microstructure analysis, the increase in YS after the two-step aging was caused by the ordering strengthening effect of κ' carbide. Further, the pre-cold rolling could introduce heterogeneous nucleation sites, inducing intragranular precipitation. The combination of the precipitation strengthening of the precipitates and deformation strengthening induced via the pre-cold rolling further increased the YS of the material. Moreover, these intragranular precipitates could improve the work hardening capability, which is the root cause of the high plasticity of materials. This process provides a novel idea for improving the performance of austenitic low-density steels.
Ping REN , Xingpin CHEN , Cunyu WANG , Feng YU , Wenquan CAO . Effects of Pre-Strain and Two-Step Aging on Microstructure and Mechanical Properties of Fe-30Mn-11Al-1.2C Austenitic Low-Density Steel[J]. Acta Metall Sin, 2022 , 58(6) : 771 -780 . DOI: 10.11900/0412.1961.2020.00509
| 1 | Suh D W, Kim N J. Low-density steels [J]. Scr. Mater., 2013, 68: 337 |
| 2 | Rana R. Low-density steels [J]. JOM, 2014, 66: 1730 |
| 3 | Howell R A, Van Aken D C. A literature review of age hardening Fe-Mn-Al-C alloys [J]. Iron Steel Technol., 2009, 6: 193 |
| 4 | Kim H, Suh D W, Kim N J. Fe-Al-Mn-C lightweight structural alloys: A review on the microstructures and mechanical properties [J]. Sci. Technol. Adv. Mater., 2013, 14: 014205 |
| 5 | Chen S P, Rana R, Haldar A, et al. Current state of Fe-Mn-Al-C low density steels [J]. Prog. Mater. Sci., 2017, 89: 345 |
| 6 | Zambrano O A. A general perspective of Fe-Mn-Al-C steels [J]. J. Mater. Sci., 2018, 53: 14003 |
| 7 | Ren P, Chen X P, Cao Z X, et al. Synergistic strengthening effect induced ultrahigh yield strength in lightweight Fe-30Mn-11Al-1.2C steel [J]. Mater. Sci. Eng., 2019, A752: 160 |
| 8 | Raabe D, Springer H, Gutierrez-Urrutia I, et al. Alloy design, combinatorial synthesis, and microstructure-property relations for low-density Fe-Mn-Al-C austenitic steels [J]. JOM, 2014, 66: 1845 |
| 9 | Springer H, Raabe D. Rapid alloy prototyping: Compositional and thermo-mechanical high throughput bulk combinatorial design of structural materials based on the example of 30Mn-1.2C-xAl triplex steels [J]. Acta Mater., 2012, 60: 4950 |
| 10 | Yao M J, Welsch E, Ponge D, et al. Strengthening and strain hardening mechanisms in a precipitation-hardened high-Mn lightweight steel [J]. Acta Mater., 2017, 140: 258 |
| 11 | Gutierrez-Urrutia I, Raabe D. Multistage strain hardening through dislocation substructure and twinning in a high strength and ductile weight-reduced Fe-Mn-Al-C steel [J]. Acta Mater., 2012, 60: 5791 |
| 12 | Welsch E, Ponge D, Hafez Haghighat S M, et al. Strain hardening by dynamic slip band refinement in a high-Mn lightweight steel [J]. Acta Mater., 2016, 116: 188 |
| 13 | Choi K, Seo C H, Lee H, et al. Effect of aging on the microstructure and deformation behavior of austenite base lightweight Fe-28Mn-9Al-0.8C steel [J]. Scr. Mater., 2010, 63: 1028 |
| 14 | Lee K, Park S J, Kang J Y, et al. Investigation of the aging behavior and orientation relationships in Fe-31.4Mn-11.4Al-0.89C low-density steel [J]. J. Alloys Compd., 2017, 723: 146 |
| 15 | Lin C L, Chao C G, Bor H Y, et al. Relationship between microstructures and tensile properties of an Fe-30Mn-8.5Al-2.0C alloy [J]. Mater. Trans., 2010, 51: 1084 |
| 16 | Frommeyer G, Brüx U. Microstructures and mechanical properties of high-strength Fe-Mn-Al-C light-weight triplex steels [J]. Steel Res. Int., 2006, 77: 627 |
| 17 | Yoo J D, Park K T. Microband-induced plasticity in a high Mn-Al-C light steel [J]. Mater. Sci. Eng., 2008, A496: 417 |
| 18 | Yoo J D, Hwang S W, Park K T. Origin of extended tensile ductility of a Fe-28Mn-10Al-1C steel [J]. Metall. Mater. Trans., 2009, 40A: 1520 |
| 19 | Chbihi A, Vincent S, Ribis J, et al. Influence of plastic deformation on the precipitation sequence in an AA6061 alloy [J]. J. Mater. Sci., 2017, 52: 6063 |
| 20 | Gazizov M, Kaibyshev R. Effect of pre-straining on the aging behavior and mechanical properties of an Al-Cu-Mg-Ag alloy [J]. Mater. Sci. Eng., 2015, A625: 119 |
| 21 | Ouyang Y, Gan X P, Li Z, et al. Microstructure evolution of a Cu-15Ni-8Sn-0.8Nb alloy during prior deformation and aging treatment [J]. Mater. Sci. Eng., 2017, A704: 128 |
| 22 | Gao N, Huttunen-Saarivirta E, Tiainen T, et al. Influence of prior deformation on the age hardening of a phosphorus-containing Cu-0.61wt.%Cr alloy [J]. Mater. Sci. Eng., 2003, A342: 270 |
| 23 | Min X H, Emura S, Zhang L, et al. Improvement of strength-ductility tradeoff in β titanium alloy through pre-strain induced twins combined with brittle Ω phase [J]. Mater. Sci. Eng., 2015, A646: 279 |
| 24 | Song Z Y, Sun Q Y, Xiao L, et al. The influence of prior cold deformation on precipitation of alpha phase and variation of hardness in Ti-10Mo-8V-1Fe-3.5Al during aging treatment [J]. J. Mater. Res., 2009, 24: 452 |
| 25 | Song B, She J, Guo N, et al. Regulating precipitates by simple cold deformations to strengthen Mg alloys: A review [J]. Materials, 2019, 12: 2507 |
| 26 | Xing J, Hou L F, Du H Y, et al. Effects of pre-deformation on the kinetics of β-Mn phase precipitation and mechanical properties in Fe-30Mn-9Al-1C lightweight steel [J]. Metall. Mater. Trans., 2019, 50A: 2629 |
| 27 | Han K H. The microstructures and mechanical properties of an austenitic Nb-bearing Fe-Mn-Al-C alloy processed by controlled rolling [J]. Mater. Sci. Eng., 2000, A279: 1 |
| 28 | Ren P, Chen X P, Mei L, et al. Intragranular brittle precipitates improve strain hardening capability of Fe-30Mn-11Al-1.2C low-density steel [J]. Mater. Sci. Eng., 2020, A775: 138984 |
| 29 | Sato K, Tagawa K, Inoue Y. Modulated structure and magnetic properties of age-hardenable Fe-Mn-Al-C alloys [J]. Metall. Trans., 1990, 21A: 5 |
| 30 | Kim C W, Kwon S I, Lee B H, et al. Atomistic study of nano-sized κ-carbide formation and its interaction with dislocations in a cast Si added FeMnAlC lightweight steel [J]. Mater. Sci. Eng., 2016, A673: 108 |
| 31 | Jin J E, Lee Y K. Effects of Al on microstructure and tensile properties of C-bearing high Mn TWIP steel [J]. Acta Mater., 2012, 60: 1680 |
| 32 | Gutierrez-Urrutia I, Raabe D. Influence of Al content and precipitation state on the mechanical behavior of austenitic high-Mn low-density steels [J]. Scr. Mater., 2013, 68: 343 |
| 33 | Park K T, Jin K G, Han S H, et al. Stacking fault energy and plastic deformation of fully austenitic high manganese steels: Effect of Al addition [J]. Mater. Sci. Eng., 2010, A527: 3651 |
| 34 | Abedi H R, Hanzaki A Z, Haghdadi N, et al. Substructure induced twinning in low density steel [J]. Scr. Mater., 2017, 128: 69 |
| 35 | Song H, Sohn S S, Kwak J H, et al. Effect of austenite stability on microstructural evolution and tensile properties in intercritically annealed medium-Mn lightweight steels [J]. Metall. Mater. Trans., 2016, 47A: 2674 |
| 36 | Han D, He J X, Guan X J, et al. Impact of short-range clustering on the multistage work-hardening behavior in Cu-Ni alloys [J]. Metals, 2019, 9: 151 |
| 37 | Han D, Wang Z Y, Yan Y, et al. A good strength-ductility match in Cu-Mn alloys with high stacking fault energies: Determinant effect of short range ordering [J]. Scr. Mater., 2017, 133: 59 |
| 38 | Zhang Y J, Han D, Li X W. A unique two-stage strength-ductility match in low solid-solution hardening Ni-Cr alloys: Decisive role of short range ordering [J]. Scr. Mater., 2020, 178: 269 |
| 39 | Wang Z W, Baker I, Cai Z H, et al. The effect of interstitial carbon on the mechanical properties and dislocation substructure evolution in Fe40.4Ni11.3Mn34.8Al7.5Cr6 high entropy alloys [J]. Acta Mater., 2016, 120: 228 |
| 40 | Song R, Ponge D, Raabe D. Improvement of the work hardening rate of ultrafine grained steels through second phase particles [J]. Scr. Mater., 2005, 52: 1075 |
| 41 | Ebeling R, Ashby M F. Dispersion hardening of copper single crystals [J]. Philos. Mag., 1966, 13A: 805 |
| 42 | Lee K, Park S J, Moon J, et al. β-Mn formation and aging effect on the fracture behavior of high-Mn low-density steels [J]. Scr. Mater., 2016, 124: 193 |
/
| 〈 |
|
〉 |