Fabrication of Nanoporous PtRuFe by Dealloying Amorphous Fe(Pt, Ru)B Ribbons and Their Methanol Electrocatalytic Properties
Received date: 2020-01-17
Revised date: 2020-05-25
Online published: 2020-06-05
Supported by
National Natural Science Foundation of China(51771039);National Natural Science Foundation of China(51171034)
The growing technological demand for high-efficiency direct methanol fuel cells (DMFCs) drives the exploration of catalysts with improved catalytic performance. Conventional pure Pt with good catalytic activity for methanol oxidation reaction (MOR) have been applied in the DMFCs for several decades, while their CO tolerance still needs to be further enhanced. Formation of nanoporous structure with a high specific surface area is an effective way to increase the catalytic efficiency by providing more active sites. Alloying suitable Fe and Ru into Pt is promising for the improvements of both catalytic activity and anti-CO poisoning. In this work, the nanoporous alloys have been fabricated by dealloying Fe65Pt10-xRuxB25 (x=0, 2, 4, atomic fraction, %) melt-spun alloy ribbons in 0.1 mol/L H2SO4 solution, and the phase structures, morphologies, chemical compositions, and magnetic properties of the melt-spun ribbons and nanoporous alloys were characterized by XRD, TEM, SEM, EDS, XPS and VSM, respectively. The electrocatalytic properties for MOR of the nanoporous alloys were examined by cycle voltammetry in 0.5 mol/L H2SO4+1.0 mol/L CH3OH solution. The results reveal that all melt-spun ribbons are fully amorphous, and nanoporous (Pt, Ru)Fe with a single-fcc phase can be obtained after dealloying. The nanoporous (Pt, Ru)Fe dealloyed from x=0 and 2 precursors possess a similar fine bicontinuous ligament/channel structure with average pore diameter and ligament size of 6~7 and 7~8 nm, respectively. Cracks can be found on the surficial nanoporous architecture for the nanoporous PtRuFe obtained from the x=4 alloy. With enriching of Ru, the oxidation peak potential of the nanoporous alloys exhibits a negative shift, and the ratio (jf/jb) of the peak current density in the forward scan (jf) to that in the backward scan (jb) increases gradually. The jf and jf/jb for the nanoporous PtRuFe dealloyed from the x=2 alloy is 0.87 mA/cm2 and 4.6, which are 1.7 and 2.7 times of those for the nanoporous PtFe, respectively, indicating the superior electrocatalytic activity for MOR and CO tolerance in comparison with the binary PtFe alloy. The improvement in electrocatalytic performance after Ru addition can be attribute to the combination of Pt/Ru bifunctional mechanism and weakened Pt-COads adsorption energy. In addition, the nanoporous PtRuFe alloys also exhibit ferromagnetic characteristic with saturation magnetization values of 0.41~0.42 T, which can be easily separated and recycled in the practical applications. This work paves the way for the development of high-performance MOR electrocatalyst.
Xiuyue XU , Yanhui LI , Wei ZHANG . Fabrication of Nanoporous PtRuFe by Dealloying Amorphous Fe(Pt, Ru)B Ribbons and Their Methanol Electrocatalytic Properties[J]. Acta Metall Sin, 2020 , 56(10) : 1393 -1400 . DOI: 10.11900/0412.1961.2020.00028
| [1] | Scofield M E, Koenigsmann C, Wang L, et al. Tailoring the composition of ultrathin, ternary alloy PtRuFe nanowires for the methanol oxidation reaction and formic acid oxidation reaction [J]. Energy Environ. Sci., 2015, 8: 350 |
| [2] | Li M Y, Zheng H J, Han G Y, et al. Facile synthesis of binary PtRu nanoflowers for advanced electrocatalysts toward methanol oxidation [J]. Catal. Commun., 2017, 92: 95 |
| [3] | Jeon M K, Won J Y, Lee K R, et al. Highly active PtRuFe/C catalyst for methanol electro-oxidation [J]. Electrochem. Commun., 2007, 9: 2163 |
| [4] | Sahin O, Kivrak H. A comparative study of electrochemical methods on Pt-Ru DMFC anode catalysts: The effect of Ru addition [J]. Int. J. Hydrogen Energy, 2013, 38: 901 |
| [5] | Rodriguez J R, Félix R M, Reynoso E A, et al. Synthesis of Pt and Pt-Fe nanoparticles supported on MWCNTs used as electrocatalysts in the methanol oxidation reaction [J]. J. Energy Chem., 2014, 23: 483 |
| [6] | Deivaraj T C, Chen W X, Lee J Y. Preparation of PtNi nanoparticles for the electrocatalytic oxidation of methanol [J]. J. Mater. Chem., 2003, 13: 2555 |
| [7] | Mondal A, De A, Datta J. Selective methodology for developing PtCo NPs and performance screening for energy efficient electro-catalysis in direct ethanol fuel cell [J]. Int. J. Hydrogen Energy, 2019, 44: 10996 |
| [8] | Lu Q Q, Huang J S, Han C, et al. Facile synthesis of composition-tunable PtRh nanosponges for methanol oxidation reaction [J]. Electrochim. Acta, 2018, 266: 305 |
| [9] | Zheng Y Y, Qiao J H, Hu J G, et al. PtIr alloy nanowire assembly on carbon cloth as advanced anode catalysts for methanol oxidation [J]. Int. J. Hydrogen Energy, 2019, 44: 20336 |
| [10] | Strasser P, Fan Q, Devenney M, et al. High throughput experimental and theoretical predictive screening of materials—A comparative study of search strategies for new fuel cell anode catalysts [J]. J. Phys. Chem., 2003, 107B: 11013 |
| [11] | Zhao Y, Hong B, Fan L Z. Electrodeposition of PtRu/MWCNTs and PtRuNi/MWCNTs and their performance in direct methanol fuel cells [J]. Acta Metall. Sin., 2013, 49: 699 |
| [11] | (赵 越, 洪 波, 范楼珍. 电沉积制备PtRu/MWCNTs和PtRuNi/MWCNTs及其在直接甲醇燃料电池中的性能 [J]. 金属学报, 2013, 49: 699) |
| [12] | Lee K R, Jeon M K, Woo S I. Composition optimization of PtRuM/C (M=Fe and Mo) catalysts for methanol electro-oxidation via combinatorial method [J]. Appl. Catal., 2009, 91B: 428 |
| [13] | Yang Y L, Mu Z Y, Fan Z, et al. Nanoporous silver via electrochemical dealloying and its superior detection sensitivity to formaldehyde [J]. Acta Metall. Sin., 2019, 55: 1302 |
| [13] | (杨玉林, 穆张岩, 范 铮等. 电化学脱合金制备纳米多孔Ag及其甲醛检测性能 [J]. 金属学报, 2019, 55: 1302) |
| [14] | Hyun J I, Kong K H, Kim W C, et al. Formation of nanoporous Cu-Ag by dealloying Mg-Cu-Y-Ag amorphous alloys and its electrocatalyst oxidation property [J]. Intermetallics, 2019, 110: 106488 |
| [15] | Liu L F, Pippel E, Scholz R, et al. Nanoporous Pt-Co alloy nanowires: Fabrication, characterization, and electrocatalytic properties [J]. Nano Lett., 2009, 9: 4352 |
| [16] | Erlebacher J, Aziz M J, Karma A, et al. Evolution of nanoporosity in dealloying [J]. Nature, 2001, 410: 450 |
| [17] | Erlebacher J. An atomistic description of dealloying: Porosity evolution, the critical potential, and rate-limiting behavior [J]. J. Electrochem. Soc., 2004, 151: C614 |
| [18] | Hodge A M, Hayes J R, Caro J A, et al. Characterization and mechanical behavior of nanoporous gold [J]. Adv. Mater., 2006, 8: 853 |
| [19] | Rizzi P, Scaglione F, Battezzati L. Nanoporous gold by dealloying of an amorphous precursor [J]. J. Alloys Compd., 2014, 586: S117 |
| [20] | Wang S S, Liu L. Fabrication of novel nanoporous copper powder catalyst by dealloying of ZrCuNiAl amorphous powders for the application of wastewater treatments [J]. J. Hazard. Mater., 2017, 340: 445 |
| [21] | Xu H J, Zhang T. Formation of ultrafine spongy nanoporous metals (Ni, Cu, Pd, Ag and Au) by dealloying metallic glasses in acids with capping effect [J]. Corros. Sci., 2019, 153: 1 |
| [22] | Ou S L, Ma D G, Li Y H, et al. Fabrication and electrocatalytic properties of ferromagnetic nanoporous PtFe by dealloying an amorphous Fe60Pt10B30 alloy [J]. J. Alloys Compd., 2017, 706: 215 |
| [23] | Luo X K, Li R, Huang L, et al. Nucleation and growth of nanoporous copper ligaments during electrochemical dealloying of Mg-based metallic glasses [J]. Corros. Sci., 2013, 67: 100 |
| [24] | Dan Z H, Qin F X, Sugawara Y, et al. Elaboration of nanoporous copper by modifying surface diffusivity by the minor addition of gold [J]. Microporous Mesoporous Mater., 2013, 165: 257 |
| [25] | Xu C X, Wang R Y, Chen M W, et al. Dealloying to nanoporous Au/Pt alloys and their structure sensitive electrocatalytic properties [J]. Phys. Chem. Chem. Phys., 2010, 12: 239 |
| [26] | Rethinasabapathy M, Kang S M, Haldorai Y, et al. Ternary PtRuFe nanoparticles supported N-doped graphene as an efficient bifunctional catalyst for methanol oxidation and oxygen reduction reactions [J]. Int. J. Hydrogen Energy, 2017, 42: 30738 |
| [27] | Frelink T, Visscher W, van Veen J A R. Particle size effect of carbon-supported platinum catalysts for the electrooxidation of methanol [J]. J. Electroanal. Chem., 1995, 382: 65 |
| [28] | Gong L Y, Yang Z Y, Li K, et al. Recent development of methanol electrooxidation catalysts for direct methanol fuel cell [J]. J. Energy Chem., 2018, 27: 1618 |
| [29] | Wang Q M, Chen S G, Li P, et al. Surface Ru enriched structurally ordered intermetallic PtFe@PtRuFe core-shell nanostructure boosts methanol oxidation reaction catalysis [J]. Appl. Catal., 2019, 252B: 120 |
| [30] | Cai Z, Kuang Y, Qi X H, et al. Ultrathin branched PtFe and PtRuFe nanodendrites with enhanced electrocatalytic activity [J]. J. Mater. Chem., 2015, 3A: 1182 |
| [31] | Tian M M, Shi S, Shen Y L, et al. PtRu alloy nanoparticles supported on nanoporous gold as an efficient anode catalyst for direct methanol fuel cell [J]. Electrochim. Acta, 2019, 293: 390 |
/
| 〈 |
|
〉 |