Microstructure and pitting corrosion resistance of UNS S32304 duplex stainless steels welded joint with plasma-arc welding (PAW) were studied by means of OM, SEM, energy dispersive X-ray spectroscopy (EDX) and potentiostatic electrochemical technique. The results show that the microstructures of the heat-affected zone (HAZ) and fusion zone differ from the base metal greatly, with ferrite fraction greater than 70\%. Furthermore, a lot of nitrides are precipitated at the interface between ferrite and austenite phases and inside the ferrite grains. Consequently, pitting corrosion resistance of the welded joint declines obviously and pitting preferentially occurs at ferrite phase in the high temperature HAZ near the fusion line.
HONG Ju-Feng
,
TAN Hua
,
CHEN Lin-Dou
,
LI Jin
,
LI Li
,
JIANG Yi-Meng
. MICROSTURE AND PITTING CORROSION RESISTANCE OF UNS S32304 DUPLEX STAINLESS STEELS WELDED JOINT WITH PLASMA-ARC WELDING[J]. Acta Metall Sin, 2011
, 47(11)
: 1445
-1449
.
DOI: 10.3724/SP.J.1037.2011.00314
[1] Cvijovic Z, Radenkovic G. Corros Sci, 2006; 48: 3887
[2] Liou R Y, Hsieh R I, Tsai WT. Corros Sci, 2002; 44: 2841
[3] Xu J L, Deng B, Sun T, Li J, Jiang Y M. Acta Metall Sin, 2010; 46: 380
(徐菊良, 邓博, 孙 涛, 李 劲, 蒋益明. 金属学报, 2010; 46: 380)
[4] Gooch T G. In: Lula ed., Duplex Stainless Steels. Metals Park, Ohio: ASM, 1983: 573
[5] Baeslack III W A, Lippold J C, Nelson D E. Weld J, 1986; 66: 241
[6] Ogawa T, Koseki T. Weld J, 1989; 68: 181
[7] Sridhar N, Flasche L H, Kolts J. Mater Perform, 1984; 23: 52
[8] Capello E, Chiarello P, Previtali B, Vedani M. Mater Sci Eng, 2003; A351: 334
[9] Deng B, Wang Z Y, Jiang Y M, Sun T, Xu J L, Li J. Corros Sci, 2009; 51: 2969
[10] Nowacki J, Lukojc A. Mater Charact, 2006; 56: 436
[11] Sathicrchinda M, Pettersson R, Wessman S, Pan J S. Corros Sci, 2010; 52: 179
[12] Nillson J O, Huhtala T, Jonsson P, Karlsson L, Wilson A. Metall Mater Trans, 1996; 27A: 2196
[13] Garzon C M, Ramirez A J. Acta Mater, 2006; 54: 3321
[14] Ramirez A J, Lippold J C, Brandi S D. Metall Mater Trans, 2003; 34A: 1575
[15] Craig E. Weld J, 1988; 67: 19
[16] Wang Y, Chen Q. J Mater Process Technol, 2002; 120: 270
[17] Urena A, Otero E, Utrilla M V, M´unez C J. J Mater Process Technol, 2007; 182: 624
[18] Deng B, Jiang Y M, Liao J X, Hao Y W, Zhong C, Li J. Appl Surf Sci, 2007; 253: 7369
[19] Tan H, Jiang Y M, Deng B, Sun T, Xu J L, Li J. Mater Charact, 2009; 60: 1049
[20] Tavares S S M, Scandian C, Pardal J M, Luz T S, Silva F J. Eng Fail Anal, 2010; 17: 1500
[21] Liou H Y, Hsieh R I, Tsai W T. Mater Chem Phys, 2002; 74: 33
[22] Weber L, Uggowitzer P J. Mater Sci Eng, 1998; A242: 222
[23] Perren R A, Suter T A, Uggowitzer P J, Weber L, Magdowski R, Bohni H, Speidel M O. Corros Sci, 2001; 43: 707
[24] Kordatos J D, Fourlaris G, Papadimitriou G. Scr Mater, 2001; 44: 401
[25] Cervo R, Ferro P, Tiziani A, Zuzzhi F. J Mater Sci, 2010; 45: 4378
[26] Ha H Y, Kwon H S. Electrochim Acta, 2007; 52: 2175