The effect of Cr addition on the transformation and the cyclic deformation characteristics in 550℃ annealed Ti-50.8Ni shape memory alloy (SMA) were investigated by differential scanning calorimetry (DSC) and tensile test. The B2→R→M/M→B2 type reversiable transformation occurred in Ti-50.8Ni alloy upon cooling/heating. After the addition of 0.3%Cr in Ti-50.8Ni alloy, the transformation type for Ti-50.8Ni-0.3Cr alloy was B2→R→M/M→R→B2, and the transformation temperatures decreased significantly. At room temperature, the phase composition was parent phase B2 for both Ti-50.8Ni and Ti-50.8Ni-0.3Cr alloys, while the former showed shape memory effect; the latter showed superelasticity. With increasing cyclic deformation number n, Ti-50.8Ni alloy evolved from shape memory effect to linear superelasticity, and its stress inducing martensitic critical stress and the accumulation residual strain increased rapidly; while Ti-50.8Ni-0.3Cr alloy evolved from incomplete superelastic to complete superelastic, and the stress-strain curve shape was stable. With increasing n, the superelastic residual strain εr decreased and the superelastic strain recovery ratio ηs of Ti-50.8Ni alloy increased, while the εr and ηs in Ti-50.8Ni-0.3Cr alloy kept at lower and higher values, respectively. The superelastic of Ti-50.8-0.3Cr alloy was stable.
YANG Jun
,
HE Zhi-Rong
,
YU Fang
,
YU Yong-Shan
,
YU Qi
,
LIU Yan
. EFFECT OF Cr ADDITION ON TRANSFORMATION AND CYCLIC DEFORMATION CHARACTERISTICS OF Ti-Ni SHAPE MEMORY ALLOY[J]. Acta Metall Sin, 2011
, 47(2)
: 157
-162
.
DOI: 10.3724/SP.J.1037.2010.00390
[1] Otsuka K, Wayman C M. Shape Memory Materials. Cambridge: Cambridge University Press, 1998: 220
[2] He Z R, Wang F, Zhou J E. Heat Treat Met, 2006; 31(9): 17
(贺志荣, 王芳, 周敬恩. 金属热处理, 2006; 31(9): 17)
[3] Kim J I, Miyazaki S. Metall Mater Trans, 2005; 36A: 3301
[4] He Z R, Wang F. Acta Metall Sin, 2010; 46: 329
(贺志荣, 王 芳. 金属学报, 2010; 46: 329)
[5] He Z R, Wang F, Wang Y S, Xia P J, Yang B. Acta Metall Sin, 2007; 43: 1293
(贺志荣, 王芳, 王永善, 夏鹏举, 杨波. 金属学报, 2007; 43: 1293)
[6] Liu A L, Sui J H, Lei Y C, Cai W, Gao Z Y, Zhao L C. J Mater Sci, 2007; 42: 5791
[7] Adharapurapu R R, Vecchio K S. Exp Mech, 2007; 47: 365
[8] Soga Y, Doi H, Yoneyama T. Mater Med, 2000; 11: 695
[9] Chen F. Mech Eng, 2009; 10: 21
(陈芳. 机械工程师, 2009; 10: 21)
[10] Shang Z J, Wang Z M, Yin G S, Zheng B Y. Rare Met Mater Eng, 2009; 38: 460
(商泽进, 王忠民, 尹冠生, 郑碧玉. 稀有金属材料与工程, 2009; 38: 460)
[11] Zhang X P, Liu H Y, Yuan B, Zhang Y P. Mater Sci Eng, 2008; A481: 170
[12] Carl P F, Alicia M O, Jeffrey T, Ken G, Hans J M. Metall Mater Trans, 2004; 35A: 2013
[13] Cho G B, Kim Y H, Hur S G, Yu C A, Nam T H. Met Mater Int, 2006; 12: 181
[14] He Z R, Wang F. Acta Metall Sin, 2008; 44: 23
(贺志荣, 王芳. 金属学报, 2008; 44: 23)
[15] Tahara M, Kim H Y, Hosoda H, Miyazaki S. Acta Mater, 2009; 57: 2461
[16] Miyazaki S, Imai T, Igo Y, Otsuka K. Metall Trans, 1986; 17A: 115
[17] Eucken S, Duering T W. Acta Metall, 1989; 37: 2245
[18] Zhao L C, Cai W, Zheng Y F. Shape Memory Effect and Superelasticity in Alloys. Beijing: National Defense Industry Press, 2002: 121
(赵连城, 蔡伟, 郑玉峰. 合金的形状记忆效应与超弹性. 北京:国防工业出版社, 2002: 121)