By means of the elastic stress-strain finite element method (FEM), the distribution features of the von Mises stress, strain energy density and the influences of the applied stress on the von Mises stress at γ/γ' phases interface and γ' phase directionally coarsening regularity in a [011] oriented single crystal nickel-based superalloy were investigated. Results show that after heat treatment, the microstructure of the superalloy consists of the cubic γ' phases embedded coherently in the γ matrix, and γ' phases arranged regularly along the <100> direction. Compared to the matrix channel near (010)γ' plane, the bigger von Mises stress are produced within the matrix channel near (001)γ' plane when the tensile stress is applied along the [011] direction. Compared to (010)γ' plane, the larger expanding lattice strain occurs on the (001)γ' plane along the [010]γ' direction under the action of the principal stress component, resulting in the Al, Ti atoms with bigger radius to be trapped by the larger strain zone, which is the main reason of promoting the γ' phase grown directionally into the strip-like rafted structure.
ZHANG Shu
,
TIAN Su-GuiShenYangTianSuGui
,
SU Yong
,
YU Hui-Chen
,
YU Xin-Fu
,
YU Li-Li
. MICROSTRUCTURE EVOLUTION AND FEM ANALYSIS OF [011] ORIENTED SINGLE CRYSTAL OF A Ni-BASED SUPERALLOY DURING TENSILE CREEP[J]. Acta Metall Sin, 2011
, 47(1)
: 61
-68
.
DOI: 10.3724/SP.J.1037.2010.00457
[1] Feng H, Biermann H, Mughrabi H. Metall Mater Trans, 2000; 31A: 585
[2] Yu X F, Tian S G, Du H Q, Yu H C, Wang M G, Shang L J, Cui S S. Mater Sci Eng, 2009; A506: 80
[3] Tien J K, Copley S M. Metall Trans, 1971; 2: 543
[4] Buffiere J Y, Ignat M. Acta Metall Mater, 1995; 43: 1791
[5] Pollock T M, Argon A S. Acta Metall Mater, 1994; 42: 1859
[6] Kuhn H A, Biermann H, Ungar T. Acta Metall Mater, 1991; 39: 2783
[7] Biermann H, Strehler M, Mughrabi H. Metall Mater Trans, 1996; 27A: 1003
[8] Tian S G, Zhang J H, Yang H C, Xu Y B, Hu Z Q. J Aeronautic Mater, 2000; 20: 1
(田素贵, 张静华, 杨洪才, 徐永波, 胡壮麒. 航空材料学报, 2000; 20: 1)
[9] Tian S G, Chen C R, Yang H C, Hu Z Q. Acta Metall Sin, 2000; 36: 465
(田素贵, 陈昌荣, 杨洪才, 胡壮麒. 金属学报, 2000; 36: 465)
[10] Tian S G, Wang M G, Yu H C, Yu X F, Li T, Qian B J. Mater Sci Eng, A527: 4458
[11] Sha Y H, Chen C R, Zhang J H, Xu Y B, Hu Z Q. Acta Metall Sin, 1999; 36: 254
(沙玉辉, 陈昌荣, 张静华, 徐永波, 胡壮麒. 金属学报, 1999; 36: 254)
[12] Zhou L, Yu X L. Trans Shenyang Ligong Univ, 2008; 27: 1
(周丽, 于晓琳. 沈阳理工大学学报, 2008; 27: 1)
[13] Nabarro F R N. Metall Mater Trans, 1996; 27A: 513
[14] Tian S G, Zhang J H, Yang H C, Hu Z Q. Mater Sci Technol, 2000; 16, 451
[15] Shui L, Yang Y H, Yu J J. Mater Mech Eng, 2009; 33: 6
(水丽, 杨彦红, 于金江. 机械工程材料, 2009; 33: 6)
[16] Shui L, Jin T, Tian S, Hu Z Q. Rare Met Mater Eng, 2009; 38: 826
(水丽, 金涛, 田素贵, 胡壮麒. 稀有金属材料与工程, 2009; 38: 826)