The high cycle fatigue properties of a new type Ni-based superalloy DZ468 were investigated in this paper. The high cycle fatigue strengths of DZ468 alloy at 900 and 760 ℃ with a ratio of stress R=-1 reach 290 and 300 MPa, respectively. The high cycle fatigue fractures of DZ468 alloy were composed of fatigue source, fatigue district and final stage. Cracks originate from surface, sub-surface and inner defect of sample. At 900 and 760 ℃, stage I and stage II crack propagation could be observed from fatigue fracture, which was caused by the combination action of planar slip, cross slip and climb of dislocations. With increasing of stress value, the crack propagation rate quickly increase. A correlation exists between the crack propagation mode and deformation mode.
Key words： Ni-based superalloy; high cycle fatigue property; fracture
LIU En-Ze . STUDY ON HIGH CYCLE FATIGUE PROPERTIES OF DZ468 SUPERALLOY[J]. Acta Metall Sin, 2010 , 46(6) : 708 -714 . DOI: 10.3724/SP.J.1037.2009.00600
[1] Yu Z F, Zheng Z, Liu E Z, Yu Y S, Zhu Y X. J Chin Soc Corros Prot, 2008; 28: 277
(于忠峰, 郑志, 刘恩泽, 于永泗, 朱耀宵. 中国腐蚀与防护学报, 2008; 28: 277)
[2] Ning L K, Zheng Z, Tan Y, Liu E Z, Tong J, Yu Y S, Wang H. Acta Metall Sin, 2009; 45: 161
(宁礼奎, 郑 志, 谭 毅, 刘恩泽, 佟健, 于永泗, 王华. 金属学报, 2009; 45: 161)
[3] Liu E Z, Sun S C, Tu G F, Zheng Z, Ning L K, Zhang L F. Acta Metall Sin, 2009; 45: 1217
(刘恩泽, 孙树臣, 涂赣峰, 郑 志, 宁礼奎, 张凌峰. 金属学报, 2009; 45: 1217)
[4] Hoffelner W. Metall Trans, 1982; 13A: 1245
[5] Sajjadi S A, Nategh S. Mater Sci Eng, 2001; A307: 158
[6] Liu Y, Yu J J, Xu Y. Mater Sci Eng, 2007; A454: 357
[7] Hoffelner W, Gudmundson P. Eng Fract Mech, 1982; 16: 365
[8] Jones B F. Int J Fatigue, 1984; 6: 75
[9] Pope D P, Ezz S S. Int Met Rev, 1984; 29: 136
[10] Sieborger D, Knake H, Glatzel U. Mater Sci Eng, 2001; A298: 26
[11] Shi C X, Yan M G, Zhu Z Q. China Aeronautical Materials Handbooks. Beijing: China Standard Press, 2001: 550
(师昌绪, 颜鸣皋, 朱之琴. 中国航空材料手册, 北京: 中国标准出版社, 2001: 550)
[12] Zheng Y R, Cai Y L, Ruan Z C, Ma S. J Aeronaut Mater, 2006; 26: 25
(郑运荣, 蔡玉林, 阮中慈, 马书. 航空材料学报, 2006; 26: 25)
[13] Zheng Y R, Wang Yu P, Xie J H, Caron P, Khan T. In: Reichman S, Duhl D N, Maurer G, Antolovich S eds., Superalloys 1988, PA: TMS, 1988: 335
[14] Zheng Y R, Cai Y L, Ruan Z C. Acta Metall Sin, 1987; 23: A430
(郑运荣, 蔡玉林, 阮中慈. 金属学报, 1987; 23: A430)
[15] Zheng Y R, Cai Y L, Wang L B. Acta Metall Sin, 1983; 19: A190
(郑运荣, 蔡玉林, 王罗宝. 金属学报, 1983; 19: A190)
[16] Zheng Y R. Chin J Aeronaut, 198; 7: 482
(郑运荣. 航空学报, 1986; 7: 482)
[17] Gell M, Leverant G R. Acta Metall, 1968; 16: 553
[18] Bowen A W, Forsyh P J EMater Sci Eng, 1981; 49: 141
[19] Forsyth P J E. Acta Metall, 1963; 11: 703
[20] Laird C. Fatigue Crack Propagation, STP415. Philadelphia: ASTM, 1967: 131
[21] Liu Y. PhD Thesis, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 2008
(刘 源. 中国科学院金属研究所博士学位论文, 沈阳, 2008)
[22] Chu Z K. PhD Thesis, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 2008
(储昭贶. 中国科学院金属研究所博士学位论文, 沈阳, 2008)
/
| 〈 |
|
〉 |