EFFECTS OF RARE EARTH ELEMENT Gd ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF NiAl-Cr(Mo)-Hf EUTECTIC ALLOY

LIANG Yong-Quan; GUO Jian-Ting; ZHOU Lan-Zhang

doi:10.3724/SP.J.1037.2009.00747

Acta Metall Sin >

2010 , Vol. 46 >Issue 5: 528 - 532

DOI: https://doi.org/10.3724/SP.J.1037.2009.00747

论文

EFFECTS OF RARE EARTH ELEMENT Gd ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF NiAl-Cr(Mo)-Hf EUTECTIC ALLOY

LIANG Yong-Quan ,
GUO Jian-Ting ,
ZHOU Lan-Zhang

Expand

1) Electric Power Research Institute of Guangdong Power Grid Corporation; Guangzhou 510080
2) Institute of Metal Research; Chinese Academy of Sciences; Shenyang 110016

Received date: 2009-11-10

Revised date: 2010-01-24

Online published: 2010-05-11

Fold

Abstract

The effects of rare earth element Gd on the microstructure and compressive properties of Ni-33Al-28Cr-5.9Mo-0.1Hf (atomic fraction, %) eutectic alloy at room temperature and 1373 K were studied. Very little amount of Gd dissolved in the NiAl and Cr(Mo) phases, and much more amount of Gd distributed in Heusler phase. Addition of Gd induced the microstructural refinement, including the decrease of the eutectic cell size and the lamellae spacing between the NiAl and Cr(Mo) plates. The proper Gd addition leads to the improvement of the compressive yield strength and ductility of the alloy at room temperature, but Gd has a little effect on the compressive properties at 1373 K. However, the Cr(Mo) phase was coarsened and distributed irregularly when 0.1 Gd (mass fraction, %) was added into the alloy, which resulted in the decrease of compressive properties at the testing temperature.

Key words： NiAl base alloy; rare earth Gd; intermetallics; microstructure; mechanical property

Cite this article

LIANG Yong-Quan , GUO Jian-Ting , ZHOU Lan-Zhang . EFFECTS OF RARE EARTH ELEMENT Gd ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF NiAl-Cr(Mo)-Hf EUTECTIC ALLOY[J]. Acta Metall Sin, 2010 , 46(5) : 528 -532 . DOI: 10.3724/SP.J.1037.2009.00747

References

[1] Noebe R D, Bowman R R, Nathal M V. Int Mater Rev, 1993; 38: 193 [2] Johnson D R, Chen X F, Oliver B F, Noebe R D, Whittenberger J D. Intermetallics, 1995; 3: 99 [3] Darolia R. JOM, 1991; 43: 44 [4] Whittenberger J D, Locci I E, Darolia R, Bowman R R. Mater Sci Eng, 1999; A268: 165 [5] Guo J T, Cui C Y, Chen Y X, Li D X, Ye H Q. Intermetallics, 2001; 9: 287 [6] Guo J T, Huai K W, Gao Q, Ren W L, Li G S. Intermetallics, 2007; 15: 727 [7] Guo J T, Yuan C, Hou J S. Acta Metall Sin, 2008; 44: 513 (}~~, ~, (. . 2008; 44: 513) [8] Fu H M, Wang H, Zhang H F, Hu Z Q. Scr Mater, 2006; 55: 147 [9] Li S, Zhao DQ, PanMX,WangWH. J Non–Cryst Solids, 2005; 351: 2568 [10] Xu X, Chen L Y, Zhang G Q, Wang L N, Jiang J Z. Intermetallics, 2007; 15: 1066 [11] Zheng Q, Cheng S, Strader J H, Ma E, Xu J. Scr Mater, 2007; 56: 161 [12] Xu J W. J Alloys Compd, 2008; 448: 331 [13] Wu X, Song D, Xia K. Mater Sci Eng, 2002; A329–331: 821 [14] Li W, Inkson B, Horita Z, Xia K. Intermetallics, 2000; 8: 519 [15] Xia K, Wu X, Song D. Acta Mater, 2004; 52: 841 [16] Xia K, Li W, Liu C. Scr Mater, 1999; 41: 67 [17] Walter J L, Cline H E. Metall Trans, 1970; 1: 1221 [18] George E P, Liu C T. J Mater Res, 1990; 5: 754 [19] Briant C L. Metall Trans, 1990; 21A: 2339 [20] Chen X F, Johnson D R, Noebe R D, Oliver B F. J Mater Res, 1995; 10: 1159 [21] Pop V, Coldea M, Neumann M, Chiuzbaian S, Todoran D. J Alloys Compd, 2002; 333: 1 [22] Fox A G, Tabbernor M A. Acta Metall Mater, 1991; 39: 669

Options

Outlines

模态框（Modal）标题

Abstract

Cite this article

References