EVOLUTION OF CORROSION PRODUCTS OF 20 CARBON STEEL IN ATMOSPHERE CONTAINING SO2
Received date: 2009-09-25
Revised date: 2009-12-21
Online published: 2010-03-11
Supported by
Supported by National Natural Science Foundation of China (No.50601012) and Higher School Key Laboratory Research Project of Jiangxi Province (No.GJJ08520})
The evolution of corrosion products of 20 carbon steel in simulated humidity atmosphere containing SO2 was investigated by means of OM, SEM, XRD and localized electrochemical impedance spectrum (LEIS). Results showed ferrous hydroxide film firstly formed on the sample surface; the film ruptured in the acidic medium, and then filaments with green heads occurred. The filaments grew along the grain boundaries and into ferrite grain. Ferrite phase was dissolved when SO2, O2 and H2O continuously penetrated into the ruptured ferrous hydroxide film and sulphate nests formed. Inside the nests FeSO4 reacted with O2 and H2O to form FeOOH, finally the cellular corrosion products formed. The cellular corrosion products and its impedance increased, and the rust layer became even and compact with further corrosion. Cellular products grew faster with the increasing SO2 concentration.
Key words： 20 carbon steel; SO2; atmospheric corrosion; growth characteristics
LIN Cui , DIAO Qing . EVOLUTION OF CORROSION PRODUCTS OF 20 CARBON STEEL IN ATMOSPHERE CONTAINING SO2[J]. Acta Metall Sin, 2010 , 46(3) : 358 -365 . DOI: 10.3724/SP.J.1037.2009.00648
[1] Cao C N. Natural Environmental Corrosion of Material in China. Beijing: Chemical Industry Press, 2005: 70
(曹楚南主编. 中国材料的自然环境腐蚀. 北京: 化学工业出版社, 2005: 70)
[2] Walter G W. Corros Sci, 1991; 32: 1331
[3] Mansfeld F, Tsai S. Corros Sci, 1980; 20: 853
[4] Cox A, Lyon L B. Corros Sci, 1994; 36: 1193
[5] Gradel T E, Frankenthal R P. J Electrochem Soc, 1990; 137: 2385
[6] Neufeld A K, Cole L S. Corrosion, 1997; 53: 788
[7] Hou W, Liang C. Corrosion, 1999; 55: 65
[8] Qu Q, YanCW, Cao C N. Corros Sci Prot Technol, 2001; 13(suppl): 432
(屈庆, 严川伟, 曹楚南. 腐蚀科学与防护技术, 2001; 13(增刊): 432)
[9] Chen H L, Wei Y. Corros Prot, 2006; 6: 284
(陈惠玲, 魏雨. 腐蚀与防护, 2006; 6: 284)
[10] Almeida E, Morcillo M, Rosales B, Marrocos M. Mater Corros, 2000; 51: 859
[11] Wang Z Y, Yu G C, Han W. J Iron Steel Res, 2003; 15: 47
(王振尧, 于国才, 韩薇. 钢铁研究学报, 2003; 15: 47)
[12] Han W, Wang J, Wang Z Y, Yu G C, Li H X. Corros Sci Prot Technol, 2003; 15: 315
(韩 薇, 汪俊, 王振尧, 于国才, 李洪锡. 腐蚀科学与防护技术, 2003; 15: 315)
[13] Yamashita M, Konishi H, Kozakura T, Mizuki J, Uchida H. Corros Sci, 2005; 47: 2492
[14] Persson D, Leygraf L. J Electrochem Soc, 1995; 142: 1459
[15] Kleber C, Weissenrieder J, Schreiner M, Leygraf C. Appl Surf Sci, 2002; 193: 245
[16] Weissenrieder J, Kleber C, Schreiner M, Leygraf C. J Electrochem Soc, 2004; 151: B497
[17] Johnson J B, Elliott P, Winterbottom M A, Wood G C. Corros Sci, 1977; 17: 691
[18] Arroyave C, Lopez F A, Morcillo M. Corros Sci, 1995; 37: 1751
[19] Misawa T, Hashimoto K, Shimodaira S. Corros Sci, 1994; 30: 283
[20] Refait P, Abdelmoula M, Genin J M R. Corros Sci, 1998; 40: 1547
[21] Cai J P, Zheng Y P, Liu S R. J Chin Soc Corros Prot, 1996; 16: 303
(蔡健平, 郑逸苹, 刘寿荣. 中国腐蚀与防护学报, 1996; 16: 303)
[22] Weissenrieder J, Leygraf C. J Electrochem Soc, 2004; 151: B165
[23] Han W, Yu G, Wang Z Y, Wang J. Corros Sci, 2007; 49: 2920
[24] Masuda H. Corrosion, 2001; 57: 99
[25] Ma Y T, Li Y, Wang F H. Mater Chem Phys, 2008; 112: 844
/
| 〈 |
|
〉 |