Evolution of Grain Boundary Character Distributions in Pb Alloy During High Temperature Annealing
Shuang Xia
上海大学材料研究所
Cite this article: 

Shuang Xia. Evolution of Grain Boundary Character Distributions in Pb Alloy During High Temperature Annealing. Acta Metall Sin, 2006, 42(2): 129-133 .

Download:  PDF(595KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  Grain boundary character distributions×(GBCD) in Pb alloy after varying kinds of thermomechanical treatments were analyzed by electron back scatter diffraction (EBSD) and orientation imaging microscopy (OIM). The frequencies of lowΣcoincidence site lattice(CSL) grain boundaries in Pb-alloy can be enhanced to more than 70% after proper cold rolling combined with annealing which was carried out at high temperature(0.9 Tm )for a very shot period of time. Together withΣ1 boundaries, the Σ3 boundaries appeared during recovering. The development of Σ3 boundaries in the process of recovery and recrystallization is the main reason for enhancing the frequencies of lowΣCSL grain boundaries. Triple junctions which contained three CSL grain boundaries could be easily find in the OIM of the specimen that had high frequencies of lowΣCSL grain boundaries, and there are specific orientation relationships among the grains assembled by the triple junctions
Key words:  Pb-alloy      GBCD      thermomechanical treatment      
Received:  10 May 2005     
ZTFLH:  TG111  

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y2006/V42/I2/129

[1] Watanabe T. Res Mech, 1984; 11(1): 47
[2] Randle V. The Role of the Coincidence Site Lattice in Grain Boundary Engineering. Cambridge: Cambridge University Press, 1996: 2
[3] Palumbo G, Erb U. MRS Bull, 1999; 24(11): 27
[4] Lee D S, Ryoo H S, Hwang S K. Mater Sci Eng, 2003; A345: 106
[5] Shimada M, Kokawa H, Wang Z J. Acta Mater, 2002; 50: 2331
[6] Lin P, Palumbo G, Erb U. Scr Metall Mater, 1995; 33: 1387
[7] Lehockey E M, Palumbo G, Lin P. Scr Mater, 1997; 36: 1211
[8] Spigarelli S, Cabibbo M, Evangelista E. Mater Sci Eng, 2003; A352: 93
[9] Lehockey E M, Palumbo G. Mater Sci Eng, 1997; A237: 168
[10] Lehockey E M, Palumbo G, Lin P. Scr Mater, 1998; 39: 353
[11] Lehockey E M, Brennenstuhl A M, Thompson I. Corros Sci, 2004; 46: 2383
[12] King W E, Schwartz A J. Scr Mater, 1998; 38: 449
[13] Palumbo G, Aust K T, Lehockey E M. Scr Mater, 1998; 38: 1685
[14] Mykura H. Grain-Boundary Structure and Kinetics. Metals Park, Ohio: American Society of Metals, 1980: 79!
[1] WANG Bin, LIU Zhenyu, Feng Jie, ZHOU Xiaoguang, WANG Guodong. PRECIPITATION BEHAVIOR AND PRECIPITATION STRENGTHENING OF NANOSCALE CEMENTITE IN CARBON STEELS DURING ULTRA FAST COOLING[J]. 金属学报, 2014, 50(6): 652-658.
[2] CAI Zhengxu WANG Weiguo FANG Xiaoying GUO Hong. EFFECT OF GRAIN SIZE ON THE GRAIN BOUNDARY CHARACTER DISTRIBUTIONS OF COLD ROLLED AND ANNEALED PURE COPPER[J]. 金属学报, 2010, 46(7): 769-774.
[3] . GRAIN BOUNDARY CHARACTER DISTRIBUTIONS OF Pb-Ca-Sn-Al ALLOY OF SOLUTION-TREATED AND PRE-AGED FOLLOWED BY STRAIN ANNEALING[J]. 金属学报, 2007, 43(5): 454-458 .
[4] CUI Jianzhong;MA Longxiang Northeast University of Technology; ShenyangDepartment of Metals Forming;Northeast University of Technology; Shenyang. GRAIN SHAPE EFFECT IN SUPERPLASTIC DEFORMATION[J]. 金属学报, 1988, 24(4): 354-361.
No Suggested Reading articles found!