CRYSTAL MORPHOLOGIES AND THE PHASES IN THE Mg–6Zn–3Y ALLOY SOLIDIFIED UNDER SUPER–HIGH PRESSURE

doi:10.3724/SP.J.1037.2011.00395

Acta Metall Sin

2011, Vol. 47

Issue (12): 1550-1554 DOI: 10.3724/SP.J.1037.2011.00395

论文

Current Issue | Archive | Adv Search

CRYSTAL MORPHOLOGIES AND THE PHASES IN THE Mg–6Zn–3Y ALLOY SOLIDIFIED UNDER SUPER–HIGH PRESSURE

LIN Xiaoping ¹, DONG Yun ¹, XU Rui ², SUN Guifang ¹, JIAO Shihui ¹

1. Department of Materials Science and Engineering, Northeastern University, Shenyang 110819
2. School of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004

Cite this article:

LIN Xiaoping DONG Yun XU Rui SUN Guifang JIAO Shihui. CRYSTAL MORPHOLOGIES AND THE PHASES IN THE Mg–6Zn–3Y ALLOY SOLIDIFIED UNDER SUPER–HIGH PRESSURE. Acta Metall Sin, 2011, 47(12): 1550-1554.

Download:

PDF(827KB)
Export: BibTeX | EndNote (RIS)

Abstract The solidification microstructure of Mg–6Zn–3Y alloy under super–high pressure was investigated by SEM and EDS. The results show that solidification microstructure of Mg–6Zn–3Y alloy under super–high pressure (GPa level) could be evidently refined and was further refined with the increase of solidification pressure. Solubility of Zn in the alloy reached up to 1.64% under 4 GPa pressure which was increased by 44% than that under the atmosphere condition. Y is insoluble in the matrix, which resulted in a new phase riched in Y and granular phases which were dispersed in the matrix. The morphology of crystal changes follow this way: bulky branch crystal→superfine branch crystal→cellular crystal, and the growth of crystal changed from branch growth to cellular growth.

Key words: Mg–6Zn–3Y alloy super–high pressure solidification dendritic crystal cellular crystal phase component

Received: 27 June 2011

Fund:

Supported by Natural Science Foundation of Hebei Province (No.E2010001398) and Natural Science Foundation of Liaoning Province (No.20112063)

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	LIN Xiao-Pin
	DONG Yuan
	XU Rui
	XUN Gui-Fang
	QIAO Shi-Hui

URL:

https://www.ams.org.cn/EN/10.3724/SP.J.1037.2011.00395 OR https://www.ams.org.cn/EN/Y2011/V47/I12/1550

[1] Qu Y D, Li R D, Yuan X G, Li C X, Xiang Q C. Foundry, 2005; 54: 539

(曲迎东, 李荣德, 袁晓光, 李晨曦, 向青春. 铸造, 2005; 54: 539)

[2] Kumar M. Physica, 1995; 212B: 391

[3] Батншeв А И, translated by Zhang J S. Crystallization of Metal and Alloys Under Pressure. Harbin: Harbin University of Techonology Press, 1987: 23

(Батншeв А И著, 张锦升译. 金属和合金在压力下结晶. 哈尔滨: 哈尔滨工业大学出版社, 1987: 23)

[4] Mi G B, Li P J, He L J. Chin J Nonferrous Met, 2009; 12:2074

(弭光宝, 李培杰, 何良菊. 中国有色金属学报, 2009; 12: 2074)

[5] Ebihara T, Uwatoko Y, Mohri N. J Magn Magn Mater, 2004; 272–276: e83

[6] Wang Z X, Lu J B, Xi Y J, Fan J W. J Alloys Compd, 2010; 492: 529

[7] Yu X F, Zhang G Z, Xiao H J, Pan A S, Jia G L, Gao Y Y. J Mater Res, 2000; 14(suppl): 141

(于溪凤, 张国志, 肖汉杰, 潘爱胜, 贾光霖, 高允彦. 材料研究学报, 2000; 14(增刊): 141)

[8] Zhang G Z, Yu X F, Wang X Y, Jia G L, Gao Y Y. Acta Metall Sin, 1999; 35: 285

(张国志, 于溪凤, 王向阳, 贾光霖, 高允彦. 金属学报, 1999; 35: 285)

[9] Yu X F, Zhang G Z, Wang X Y. J Mater Sci, 1999; 34: 4149

[10] Li R D, Huang Z P, Bai Y H, Yu H P. Spec Cast Nonferrous Alloys, 2003; (6): 16

(李荣德, 黄忠平, 白彦华, 于海朋. 特种铸造及有色合金, 2003; (6): 16)

[11] Wu R I, Wide G, Perepezko J H. J Mater Sci Technol, 2001; 301A: 12

[12] Yao W J, Wang N, Wei B. Mater Sci Eng, 2003; A344: 10

[13] Chen Z W, Jiang Y M, Chai Y. Foundry, 2009; 58: 887

(陈忠伟, 江雅民, 柴艳. 铸造, 2009; 58: 887)

[14] Xu R, Zhao H, Li J, Liu R, Wang W K. Mater Letts, 2006; 60: 783

[15] Kaibyshev F M R, Lesuer D R, Nieh T G. Mater Sci Eng, 2003; A342: 169

[16] Bao Y Q, Yuan C S, Bai Y H, Li R D. Foundry, 2011; 60: 533

(包艳青, 袁朝圣, 白彦华, 李荣德. 铸造, 2011; 60: 533)

[17] Liu C M, Zhu X R, Zhou H T. Magnesium Alloy Phase Atlas. Changsha: Central South University Press, 2007: 334

(刘楚明, 朱秀荣, 周海涛. 镁合金相图集. 长沙: 中南大学出版社, 2007: 334)

[18] Zhou H T, Zhang Z D, Liu C M, Wang Q W. Mater Sci Eng, 2007; A445–446: 1

[19] Yasuo F. J Phys: Condens Mater, 2002; 12: 10727

[20] Xu R, Zhao H, Li J, Liu R, Wang W K. Mater Lett, 2006; 60: 783

[21] Wang Z L. PhD Thesis, Harbin Institute of Technology, 2007

(王振玲. 哈尔滨工业大学博士学位论文, 2007)

[22] Li R D, Cao X S, Qu Y D, Xie Y, Li R X, Tian C. Chin J Nonferrous Met, 2009; 19: 1570

(李荣德, 曹修生, 曲迎东, 谢尧, 李润霞, 田畅. 中国有色金属学报, 2009; 19: 1570)

[23] Sun S H, Li J, Xu R, Zhao H L, Liu R P. Chin J High Pressure Phys, 2008; 22: 434

(孙淑华, 李杰, 徐瑞, 赵海丽, 刘日平. 高压物理学报, 2008; 22: 434)

[24] Wang W K. Chin J High Pressure Phys, 1989; 3: 257

(王文魁. 高压物理学报, 1989; 3: 257)

[1]	ZHAO Lining LIN Xin HUANG Weidong. FORMATION AND EVOLUTION OF THE NON-DENDRITIC MORPHOLOGY IN UNDERCOOLING MELT WITH LOWER SHEARING RATE[J]. 金属学报, 2011, 47(4): 403-409.
[2]	. Enhanced plasticity of bulk metallic glass composite containing as-cast in situ formed ductile phase dendrite dispersions[J]. 金属学报, 2006, 42(3): 331-336 .
[3]	REN Zhifeng;ZHANG Chengfu Huazhong University of Science and Technology; WuhanDivision of Casting; Huazhong University of Science and Technology; Wuhan. TRANSFORMATION OF CRYSTAL MORPHOLOGY OF EUTECTIC COMPOSITE-IN-SITU[J]. 金属学报, 1988, 24(4): 365-367.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed