EFFECTS OF ALUMINIUM ON COMMERCIAL GRAIN-ORIENTED 3% Si-IRON WITH MnS AS THE MAIN SECOND PHASE
Res. GP. of Silicon-Iron; Peking Institute of Iron and Steel Research
Cite this article: 

Res. GP. of Silicon-Iron; Peking Institute of Iron and Steel Research. EFFECTS OF ALUMINIUM ON COMMERCIAL GRAIN-ORIENTED 3% Si-IRON WITH MnS AS THE MAIN SECOND PHASE. Acta Metall Sin, 1977, 13(z1): 80-161.

Download:  PDF(8495KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The effects of aluminium on the hot-rolling structure and texture, primaryrecrystallization, secondary recrystallization and magnetic properties of commercialgrain-oriented 3% Si-iron with MnS as the main second phase have been inve-stigated. It was found that within the range of 0.007 to 0.040% aluminiumcontent (acid soluble) in silicon iron, the magnetic induction of the product,B_(10), could reach 18000 G until the temperature of the slab reheating prior tohot rolling was about 1250℃. With soluble aluminium contents outside thisrange, the value of B(10) was sharply decreased as the slab reheating temperaturewas lowered. The deformation structures and textures of the hot rolled sheetsin mid-thickness layer varied with the variations of the soluble aluminium con-tents in silicon iron as shown by the corresponding changes of structures afterprimary and secondary recrystallization. Although the role of aluminium playedin the silicon iron may be traced back prior to the hot rolling, it appears thataluminium mainly influences the deformation, dynamic precipitation of the secondphase and dynamic recrystallization processes of the material during hot rolling.Further studies are necessary to clarify the exact mechanism involved in theeffect of aluminium in grain-oriented 3% Si-iron.
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1977/V13/Iz1/80

[1] Littmann, F., Met. Trans., 6A (1975) , 1041.
[2] 钢铁研究院硅钢组,硫化锰和氮化铝夹杂对冷轧取向硅钢片性能的影响,1975,待发表工作.
[3] 熊井洁,日本特许出願公开昭47-25250.
[4] Tassy-Betz, E., Metallography, 7 (1974) , 91.
[5] Paxton, W. S. and Nilan, T. G., J. Appl. Phys., 26 (1955) , 994.
[6] 松冈孝,铁钢,52(1966) ,1179.
[7] 钢铁研究院物理室电子显微镜组,冷轧取向硅钢片中硫化锰析出过程和位错组态的电子衍衬观察,1976,待发表.
[8] Shilling, J. W. and House, G. L., IEEE Trans., MAG-10 (1974) , 195.
[9] 松村治,鹤冈一夫,日本金属学会志,38(1974) ,708.
[10] Matsumato, F. et al., 20th Inter. Conf. on Magnetism and Magnetic Materials, 1974, San Francisco, p. 116.
[11] Michalak. J. T. and Schoone, R. D., Trans. AIME, 242 (1968) , 1149.

[12] Hutchinson, W. B., "Development of Textues in Recrystallization", Preprint, International Confrence on Recrystallization in the Control of Microstructure, 1973, London.
[13] Byrne, J. G., Recovery, Recrystallization and Grain Growth, Macmillan, New York, 1965.
[14] Littmann, F., Trans. AIME., 245 (1969) , 2217.
[15] 东正则,日本特许出愿公开昭50-99914.
[16] 植野清,高田敏彦,日本特许出愿公开昭48-46511.e
No related articles found!
No Suggested Reading articles found!