AlSi10Mg的激光选区熔化成形研究
作者简介 张文奇,男,1991年生,硕士
收稿日期: 2016-10-24
网络出版日期: 2017-05-10
基金资助
国家自然科学基金项目No.61475056, 中央高校基本科研业务费专项资金项目No.2016XYZD00, 湖北省自然科学基金重点项目No.2014CFA049, 以及武汉光电国家实验室主任基金项目
Study on the Selective Laser Melting of AlSi10Mg
Received date: 2016-10-24
Online published: 2017-05-10
Supported by
Supported by National Natural Science Foundation of China (No.61475056), Fundamental Research Funds for the Central Universities (No.2016XYZD00), Natural Science Foundation of Hubei Province (No.2014CFA049) and Director Fund of Wuhan National Laboratory for Optoelectronics
利用激光选区熔化(selective laser melting, SLM)成形技术对AlSi10Mg铸造铝合金的成形进行了工艺研究,获得了致密的成形,并对其沉积态和热处理态试样进行了静态拉伸性能测试和显微组织分析。结果表明：对于AlSi10Mg, 其SLM沉积态的常温拉伸强度远高于铸件标准,延伸率与铸态相当;退火工艺对SLM试样的组织及力学性能有着重要的影响,随着退火温度的提高,试样微观组织发生改变,在300 ℃、2 h退火工艺下,原本均匀分布的颗粒状Si聚集长大为针状,使得试样的强度下降,延伸率升高。抗拉强度由沉积态的507~518 MPa下降到378~406 MPa,延伸率由沉积态的3.0%~3.5%增加到6.5%~9.0%。
张文奇 , 朱海红 , 胡志恒 , 曾晓雁 . AlSi10Mg的激光选区熔化成形研究[J]. 金属学报, 2017 , 53(8) : 918 -926 . DOI: 10.11900/0412.1961.2016.00472
The growing interest for a wide range of usable Al alloy parts with complex shape in industrial field makes selective laser melting (SLM) stand out as a new technology for rapid prototyping manufacturing. The objective of this work is to investigate AlSi10Mg cast aluminum alloy manufacturing by SLM. The investigation involved the influence of process parameters on the relative density and the influence of heat treatment on the microstructure and mechanical properties. High density and performance were achieved. The results show that the tensile strength of the SLMed AlSi10Mg is much higher than that of press wrought AlSi10Mg, but the elongation is as almost same as that of the press wrought AlSi10Mg. The heat treatment has a significant effect on the mechanical properties and microstructure of SLMed AlSi10Mg parts. The mechanical properties changes with the annealing temperature. Compared with the mechanical properties without annealing process, the tensile strength decreases from 507~518 MPa to 378~406 MPa and the elongation increases from 3.0%~3.5% to 6.5%~9.0% when the annealing temperature is 300 ℃ and the soap time is 2 h because of the changes in the morphology and distribution of the Si.
Key words： AlSi10Mg; selective laser melting; mechanical property; heat treatment
| [1] | Zhang H, Zhu H H, Qi T, et al.Selective laser melting of high strength Al-Cu-Mg alloys: Processing, microstructure and mechanical properties[J]. Mater. Sci. Eng., 2016, A656: 47 |
| [2] | Chen R, Xu Q Y, Liu B C.Modelling investigation of precipitation kinetics and strengthening for needle/rod-shaped precipitates in Al-Mg-Si alloys[J]. Acta Metall. Sin., 2016, 52: 987(陈瑞, 许庆彦, 柳百成. Al-Mg-Si合金中针棒状析出相时效析出动力学及强化模拟研究[J]. 金属学报, 2016, 52: 987) |
| [3] | Heinz A, Haszler A, Keidel C, et al.Recent development in aluminium alloys for aerospace applications[J]. Mater. Sci. Eng., 2000, A280: 102 |
| [4] | Calignano F.Design optimization of supports for overhanging structures in aluminum and titanium alloys by selective laser melting[J]. Mater. Des., 2014, 64: 203 |
| [5] | Kanagarajah P, Brenne F, Niendorf T, et al.Inconel 939 processed by selective laser melting: Effect of microstructure and temperature on the mechanical properties under static and cyclic loading[J]. Mater. Sci. Eng., 2013, A588: 188 |
| [6] | Yadroitsev I, Smurov I.Selective laser melting technology: From the single laser melted track stability to 3D parts of complex shape[J]. Phys. Procedia, 2010; 5: 551 |
| [7] | Hu Z H, Zhu H H, Zhang H, et al.Experimental investigation on selective laser melting of 17-4PH stainless steel[J]. Opt. Laser Technol., 2017, 87: 17 |
| [8] | Zhang D Y.Model manufacturing process from aluminum alloys using selective laser melting[J]. Chin. J. Lasers, 2007, 34: 1700(张冬云. 采用区域选择激光熔化法制造铝合金模型[J]. 中国激光, 2007, 34: 1700) |
| [9] | Dai D H, Gu D D.Tailoring surface quality through mass and momentum transfer modeling using a volume of fluid method in selective laser melting of TiC/AlSi10Mg powder[J]. Int. J. Mach. Tools Manuf., 2015, 88: 95 |
| [10] | Wei K W, Wang Z M, Zeng X Y.Influence of element vaporization on formability, composition, microstructure, and mechanical performance of the selective laser melted Mg-Zn-Zr components[J]. Mater. Lett., 2015, 156: 187 |
| [11] | Aboulkhair N T, Maskery I, Tuck C, et al.On the formation of AlSi10Mg single tracks and layers in selective laser melting: Microstructure and nano-mechanical properties[J]. J. Mater. Process. Technol., 2016, 230: 88 |
| [12] | Buchbinder D, Meiners W, Pirch N, et al.Investigation on reducing distortion by preheating during manufacture of aluminum components using selective laser melting[J]. J. Laser Appl., 2014, 26: 012004 |
| [13] | Li Y L, Gu D D.Parametric analysis of thermal behavior during selective laser melting additive manufacturing of aluminum alloy powder[J]. Mater. Des., 2014, 63: 856 |
| [14] | Kempen K, Thijs L, Yasa E, et al.Process optimization and microstructural analysis for selective laser melting of AlSi10Mg [A]. Solid Freeform Fabrication: An Additive Manufacturing Conference[C]. Austin: University of Texas, 2011: 484 |
| [15] | Louvis E, Fox P, Sutcliffe C J.Selective laser melting of aluminium components[J]. J. Mater. Process. Technol., 2011, 211: 275 |
| [16] | Thijs L, Kempen K, Kruth J P, et al.Fine-structured aluminium products with controllable texture by selective laser melting of pre-alloyed AlSi10Mg powder[J]. Acta Mater., 2013, 61: 1809 |
| [17] | Lam L P, Zhang D Q, Liu Z H, et al.Phase analysis and microstructure characterisation of AlSi10Mg parts produced by selective laser melting[J]. Virtual Phys. Prototyp., 2015, 10: 207 |
| [18] | Brandl E, Heckenberger U, Holzinger V, et al.Additive manufactured AlSi10Mg samples using selective laser melting (SLM): Microstructure, high cycle fatigue, and fracture behavior[J]. Mater. Des., 2012, 34: 159 |
| [19] | Kempen K, Thijs L J, Van Humbeeck J, et al.Mechanical properties of AlSi10Mg produced by selective laser melting[J]. Phys. Procedia, 2012, 39: 439 |
| [20] | Aboulkhair N T, Tuck C, Ashcroft I, et al.On the precipitation hardening of selective laser melted AlSi10Mg[J]. Metall. Mater. Trans., 2015, 46A: 3337 |
| [21] | Zhang H, Zhu H, Nie X, et al.Effect of zirconium addition on crack, microstructure and mechanical behavior of selective laser melted Al-Cu-Mg alloy[J]. Scr. Mater., 2017, 134: 6 |
| [22] | Guan K, Wang Z M, Gao M, et al.Effects of processing parameters on tensile properties of selective laser melted 304 stainless steel[J]. Mater. Des., 2013, 50: 581 |
| [23] | Read N, Wang W, Essa K, et al.Selective laser melting of AlSi10Mg alloy: Process optimisation and mechanical properties development[J]. Mater. Des., 2015, 65: 417 |
| [24] | Rosenthal I, Stern A, Frage N.Microstructure and mechanical properties of alsi10mg parts produced by the laser beam additive manufacturing (AM) technology[J]. Metall. Microstruct. Anal., 2014, 3: 448 |
| [25] | Li W, Li S, Liu J, et al.Effect of heat treatment on AlSi10Mg alloy fabricated by selective laser melting: microstructure evolution, mechanical properties and fracture mechanism[J]. Mater. Sci. Eng., 2016, A663: 116 |
/
| 〈 |
|
〉 |