CORROSION BEHAVIOR OF GH3535 SUPERALLOY IN FLiNaK MOLTEN SALT

  • Tao LIU ,
  • Jiasheng DONG ,
  • Guang XIE ,
  • Yisheng WANG ,
  • Hui LI ,
  • Zhijun LI ,
  • Xingtai ZHOU ,
  • Langhong LOU
Expand
  • 1 School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024
    2 Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016
    3 Power Branch, AVIC China National South Aviation Industry Co., Ltd., Zhuzhou 412002
    4 Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800

Online published: 2015-06-01

摘要

将带Al2O3涂层和无涂层的GH3535合金在FLiNaK熔盐中进行全浸腐蚀实验, 利用SEM, EDS, XRD等手段研究了有无Al2O3涂层的GH3535合金在熔盐中的腐蚀行为. 结果表明, 有无涂层的GH3535合金在700 ℃的FLiNaK熔盐中的腐蚀行为均表现出Cr, Mo的脱熔腐蚀特征, 无涂层合金表现出显著的沿晶腐蚀特征. Al2O3涂层并未提高合金的抗腐蚀性能, Al2O3涂层在FLiNaK熔盐中发生了溶解, 并与因Al2O3溶解脱落而裸露出来的合金表面形成腐蚀电池, 从而加速了GH3535合金的腐蚀.

本文引用格式

刘涛,董加胜,谢光,王义胜,李辉,李志军,周兴泰,楼琅洪 . GH3535合金在FLiNaK熔盐中的腐蚀行为[J]. 金属学报, 2015 , 51(9) : 1059 -1066 . DOI: 10.11900/0412.1961.2015.00132

Abstract

As one of the most promising next generation reactors, the molten salt breeder reactor (MSBR) with excellent inherence security has attracted more and more attentions in recent years due to energy shortage and the security problem of traditional nuclear reactor. The most significant service characteristic of the structural material used in MSBR is the existence of FLiNaK molten salt compared with other nuclear reactors. FLiNaK molten salt is very corrosive to the structural material in the reactor, and affects the safety operation of nuclear power plants. A polycrystalline Ni-Mo-Cr-Fe superalloy was developed and used as an important structural material in MSBR at Oak Ridge National Laboratory (ORNL), but the corrosion mechanism of the alloy in FLiNaK molten salt has not been determined since the study terminated in 1970' s as some politic reasons. Alloy served in harsh environments, often using protective coating to improve the corrosion properties. While few works about the coating corrosion resistance in FLiNaK molten salt were reported at present. Al2O3 and Cr2O3 coatings usually have excellent corrosion resistance in molten salt, such as sulphate, nitrate and halide molten salt. But, whether the oxide film has corrosion resistance in FLiNaK molten salt has not been determined. In this work, the corrosion mechanism of alloy in FLiNaK molten salt was studied by using immersion corrosion experiment through the method of SEM, EDS and XRD. The influence of Al2O3 coating on corrosion resistance in FLiNaK molten salt was also investigated. The results show that the Al2O3 coating does not affect the exsolution corrosion characteristics of Cr and Mo elements in FLiNaK molten salt at 700 ℃ for 400 h. The different is that naked alloy exhibits intergranular corrosion characteristic, and the alloy with Al2O3 coating exhibits spot corrosion characteristic. The Al2O3 coating cannot improve the corrosion resistance of the alloy in FLiNaK molten salt. The Al2O3 film dissolved in molten salt and resulted in the exposure of the alloy surface. The corrosion rate was increased since the formation of corrosion cell between oxide film and the exposed alloy surface.

参考文献

[1] Guerrieri C, Cammi A, Luzzi L. Prog Nucl Energ, 2013; 67: 56
[2] Zou S L, Zou Y. J Univ South China (Soc Sci Ed), 2011; 12(2): 1 (邹树梁, 邹 旸. 南华大学学报(社会科学版), 2011; 12(2): 1)
[3] Zanetti M, Cammi A, Fiorina C, Luzzi L. Prog Nucl Energy, 2015; 83: 82
[4] Jér?me S, Michel A, Ondrej B, Sylvie D, Olga F, Véronique G, Daniel H, David H, Victor I, Jan L K, Lelio L, Elsa M L, Jan U, Ritsuo Y, Dai Z. Prog Nucl Energy, 2014; 77: 308
[5] Rosenthal M W, Kasten P R, Briggs R B. Nucl Appl Technol, 1970; 8: 107
[6] Manly W D, Coobs J H, De Van J H, Douglas D A, Inouye H, Patriarca P, Roche T K, Scott J L. Prog Nucl Energy, 1960; 4: 164
[7] Wang Y M. J Chin Soc Corros Prot, 1981; 1: 64 (罔毅民. 中国腐蚀与防护学报, 1981; 1: 64)
[8] Nobuya I, Yukio M, Kazuo F, Yoshio K, Hiroshi K. Trans JWRI, 1980; 9: 117
[9] Kondo M, Nagasaka T, Xu Q, Muroga T, Sagara A, Noda N, Ninomiya D, Nagura M, Suzuki A, Terai T, Fujii N. Fusion Eng Des, 2009; 84: 1081
[10] Olson L C, Ambrosek J W, Sridharan K, Anderson M H, Allen T R. J Fluorine Chem, 2009; 130: 67
[11] Cho S H, Park S B, Kang D S, Jeong M S, Park H, Hur J M, Lee H S. J Nucl Mater, 2010; 399: 212
[12] Rahman A, Chawlab V, Jayaganthan R, Chandra R, Ambardar R. Mater Chem Phys, 2011; 126: 253
[13] Dutta R S, Yusufali C, Paul B, Majumdar S, Sengupta P, Mishra R K, Kaushik C P, Kshirsagar R J, Kulkarni U D, Dey G K. J Nucl Mater, 2013; 432: 72
[14] Ma J, Jiang S M, Gong J, Sun C. Corros Sci, 2012; 58: 251
[15] Firouzi A, Shirvani K. Corros Sci, 2010; 52: 3579
[16] Zheng D Y, Zhu S L, Wang F H. Surf Coat Technol, 2006; 200: 5931
[17] Phahle A M, Hill A E, Calderwood J H. Thin Solid Films, 1974; 22: 67
[18] Dasher B E, Farmer J, Ferreira J, Caro M S, Rubenchik A, Kimura A. J Nucl Mater, 2011; 419: 15
[19] Liu T, Dong J S, Wang L, Li Z J, Zhou X T, Lou L H, Zhang J. J Mater Sci Technol, 2015; 31: 269
[20] Ouyang F Y, Chang C H, You B C, Yeh T K, Kai J J. J Nucl Mater, 2013; 437: 201
[21] Tyreman C J. PhD Dissertation, University of Manchester, Manchester, UK, 1986
[22] Olson L C. PhD Dissertation, University of Wisconsin-Madison, Madison, USA, 2009
[23] Fu G F, Wang J, Kang J. Trans Nonferr Met Soc China, 2008; 18: 743
[24] Dreveton A. Procedia Eng, 2012; 46: 255
[25] Cao C N. Principles of Electrochemistry of Corrosion. Beijing: Chemical Industry Press, 2008: 104 (曹楚南. 腐蚀电化学原理. 北京: 化学工业出版社, 2008: 104)
文章导航

/