定向凝固Ti-52%Al合金热稳定处理及其对微观组织的影响*
刘国怀, 男, 蒙古族, 1985年生, 博士生
收稿日期: 2013-07-25
修回日期: 2013-12-04
网络出版日期: 2014-03-20
基金资助
*国家自然科学基金项目 51071062, 51274077和51271068, 国家重点基础研究发展计划项目2011CB605504, 华中科技大学磨具技术国家重点实验室开放基金项目 2011-P03, 中央高校基本科研业务费项目 HIT.NSRIF.2013002资助
THERMAL STABILIZATION TREATMENT AND THE EFFECT ON THE MICROSTRUCTURE IN DIRECTIONALLY SOLIDIFIED Ti-52%Al ALLOY
Received date: 2013-07-25
Revised date: 2013-12-04
Online published: 2014-03-20
Supported by
Supported by National Natural Science Foundation of China (Nos.51071062, 51274077 and 51271068), National Basic Research Program of China (No.2011CB605504), Open Project of State Key Lab of Mold and Die Technology of Huazhong University of Science and Technology (No.2011-P03) and Fundamental Research Funds for the Central Universities (No.HIT.NSRIF.2013002).
刘国怀 , 张元 , 李新中 , 陈瑞润 , 苏彦庆 , 郭景杰 , 傅恒志 . 定向凝固Ti-52%Al合金热稳定处理及其对微观组织的影响*[J]. 金属学报, 2014 , 50(3) : 329 -336 . DOI: 10.3724/SP.J.1037.2013.00444
以Ti-52%Al合金为研究对象, 在Bridgman定向凝固炉中进行不同时间的热稳定处理实验及相关的定向凝固实验, 研究了定向凝固前糊状区的形成及其微观组织演化、界面形态和溶质分布, 并考察了热稳定处理对定向凝固组织的影响. 结果表明, 试样熔化后形成了由α相晶粒、晶粒间富Al液滴和液相通道组成的糊状区, 糊状区前沿为完全液相区. 随着热稳定处理时间的增加, 糊状区内α晶粒逐渐融合且沿温度梯度方向定向排布, 富Al液滴和液相通道逐渐消失, 固/液界面变得光滑平整. 热稳定处理时间足够长时, 糊状区内为单一的α相, 溶质Al的成分在生长方向近似沿着α固相线变化. 根据溶质守恒计算得出完全液相区内溶质Al含量为52.21%, 高于试样原始成分, 与实验测量结果相一致. 进一步研究热稳定处理对后续定向凝固组织的影响, 发现合理的热稳定处理时间(≥30 min)确保了定向凝固启动界面处存在稳定的温度场和浓度场, 柱状晶沿生长方向能够平行并列生长, 试样具有良好的定向效果.
| [1] | Mullins C W, Sekerka R F. Appl Phys, 1964; 35: 444 |
| [2] | Geng X G, Cheng G, Fu H Z. Acta Metall Sin, 2002; 38: 225 |
| [2] | (耿兴国, 陈 光, 傅恒志. 金属学报, 2002; 38: 225) |
| [3] | Bosenberg U, Buchmann M, Rettenmayr M. J Cryst Growth, 2007; 304: 281 |
| [4] | Thi H N, Drevet B, Debierre J M. J Cryst Growth, 2003; 253: 539 |
| [5] | Buchmann M, Rettenmayr M. J Cryst Growth, 2005; 284: 544 |
| [6] | Su Y Q, Liu D M, Li X Z, Luo L S, Guo J J, Fu H Z. J Cryst Growth, 2010; 312: 2441 |
| [7] | Umeda T, Okane T, Kurz W. Acta Mater, 1996; 44: 4209 |
| [8] | Trivedi R, Park J S. J Cryst Growth, 2002; 235: 572 |
| [9] | Lo T S, Dobler S, Plapp M, Karma A, Kurz W. Acta Mater, 2003; 51: 599 |
| [10] | Asta M, Beckman C, Karma A. Acta Mater, 2009; 57: 941 |
| [11] | Liu G H, Li X Z, Su Y Q, Liu D M, Guo J J, Fu H Z. J Alloys Compd, 2012; 541: 275 |
| [12] | Allen D J, Hunt J D. Metall Trans, 1976; 7A: 767 |
| [13] | Liu D M, Su Y Q, Li X Z, Luo L S, Guo J J, Fu H Z. J Cryst Growth, 2010; 312: 3658 |
| [14] | Liu C. PhD Dissertation, Harbin Institute of Technology, 2006 |
| [14] | (刘 畅. 哈尔滨工业大学博士学位论文, 2006) |
| [15] | Luo W Z, Shen J, Li Q L, Man W W, Fu H Z. Acta Metall Sin, 2007; 43: 897 |
| [15] | (罗文忠, 沈 军, 李庆林, 满伟伟, 傅恒志. 金属学报, 2007; 43: 897) |
/
| 〈 |
|
〉 |