P92钢中δ铁素体对700和750℃时效析出相成分和体积分数的影响

  • 彭志方 蔡黎胜 彭芳芳 党莹樱 陈方玉
展开
  • 1) 武汉大学动力与机械学院, 武汉 430072
    2) 东方锅炉(集团)股份有限公司材料研究所, 自贡 643001
    3) 武汉钢铁(集团)公司研究院检测所, 武汉 430080
彭志方, 男, 1954年生, 教授, 博士

收稿日期: 2012-02-22

  修回日期: 2012-04-28

  网络出版日期: 2012-11-11

基金资助

国家自然科学基金项目50674072和东方锅炉(集团)股份有限公司2009-2011科技项目资助

 EFFECT OF δ-FERRITE ON THE COMPOSITION AND VOLUME FRACTION OF PRECIPITATES IN P92 STEEL AGED AT 700 AND 750℃

  • PENG Zhifang CAI Lisheng PENG Fangfang DANG Yingying CHEN Fangyu
Expand
  • 1) School of Power and Mechanical Engineering, Wuhan University, Wuhan 430072
    2) Materials Research Department, Dong Fang Boiler Group Corp. Ltd., Zigong 643001
    3) Research Institute of Wuhan Iron and Steel Company Ltd., Wuhan 430080

Received date: 2012-02-22

  Revised date: 2012-04-28

  Online published: 2012-11-11

Supported by

Supported by National Natural Science Foundation of China (No.50674072) and Scientific Research Project of Dong Fang Boiler Group Corp. Ltd., 2009-2011

摘要

将有、无δ铁素体的P92钢管样在700和750℃分别时效1000, 3000和5000 h, 采用电子探针-X射线能谱分析(EPMA--EDS)和复相分离技术(MPST)研究了δ铁素体对时效析出M23C6及Laves相体积分数及相成分的影响. 结果表明, 在时效过程中, δ铁素体的存在促进了M23C6及 Laves沿δ铁素体的界面析出, 发生聚集与粗化, 并为该过程提供Cr, Mo和W; 在无δ铁素体的P92钢管样中, 不同温度下, M23C6体积分数随时效时间的变化速率不同; 在有δ铁素体的P92钢管样中, 温度降低促进了Laves体积分数的增加, 升高温度则有利于M23C6体积分数的增加. 此外, 提高时效温度和延长时效时间可促进2种析出相的粗化.

关键词: P92钢; δ铁素体; M23C6; Laves

本文引用格式

彭志方 蔡黎胜 彭芳芳 党莹樱 陈方玉 . P92钢中δ铁素体对700和750℃时效析出相成分和体积分数的影响[J]. 金属学报, 2012 , 48(11) : 1315 -1320 . DOI: 10.3724/SP.J.1037.2012.00086

Abstract

Using the as-received P92 steel pipe steel samples with/without δ-ferrite as objects and EPMA-EDS+MPST (multiphase separation technique), this work investigated the effects of δ-ferrite on the volume fraction and< composition of M23C6 and Laves phases precipitated in the ageing treatment at 700 and 750℃ for 1000, 3000 and 5000 h, respectively. The results are as follows. The existence of δ-ferrite promoted aggregation and coarsening of M23C6 and Laves particles precipitated along boundaries with its neighboring lath martensite at the expense of consuming Cr, Mo and W in δ-ferrite during the ageing treatments. Varying rate of the volume fraction of M23C6 with the ageing time for the samples without δ-ferrite would chang at different ageing temperatures, and also the volume fraction of Laves phase would increase with decreasing ageing temperature for the samples with δ-ferrite. Owing to a few amount of Laves formed at higher temperature, the volume fraction of M23C6 increased in the samples with δ-ferrite. And increasing ageing temperature and time stimulated the coarsening of particles precipitated in the pipe samples investigated. It is expected that the related information from this study on the effects of existence of δ-ferrite on the microstructural stability and high temperature properties of P92 can be used as a reference when needed.

Key words: P92 steel; δ-ferrite; M23C6; Laves

参考文献

[1] Abe F. Sci Technol Adv Mater, 2008; 9: 1

[2] Maruyama F. ISIJ Int, 2001; 6: 612

[3] Yang F. In: Chinese Society for Electrical Engineering, ed., Symposium on Localization of A New Steel For 600 MW/1000 MW Ultra–Supercritical Units, Zibo: EPTCINA.CN, 2009: 1

(杨 富. 见: 中国电机工程学会主编, 600 MW/1000 MW超超临界机组新型钢

国产化研讨会报告文集, 淄博: 中国电力科技网, 2009: 1)

[4] Ryu S H, Yu J. Metall Mater Trans, 1998; 29A: 1573

[5] Faulkner R G, Williams J A, Sanchez E G, Marshall A W. Mater Sci Technol, 2003; 19: 347

[6] Yoshizawa M, Igarashi M. Int J Pres Ves Pip, 2007; 84: 37

[7] Kimura K, Yamaoka S. Mater Sci Eng, 2004; A387–389: 628

[8] Cai G J, Andren H O, Svensson L E. Metall Mater Trans, 1997; 28A: 1417

[9] Maruyama K, Sawada K, Koike J. ISIJ Int, 2001; 41: 641

[10] Tchizhik A A, Tchizhik T A, Tchizhik A A. J Metall Process Technol, 1998; 77: 226

[11] Kishore R, Singh R N, Sinha T K, Kashyap B P. J Nucl Mater, 1992; 195: 198

[12] Mayr P, Palmer T A, Elmer J W, Specht E D, Allen S M. Metall Mater Trans, 2010; 41A: 2010

[13] Anderko K, Schafer L, Materna–Morris E. J Nucl Mater, 1991; 179–181: 492

[14] Onoro J. J Mater Process Technol, 2006; 180: 137

[15] Sawada K, Kushima H, Kimura K. ISIJ Int, 2006; 46: 769

[16] Vijayalakshmi M, Saroja S, Thomas Paul V, Mythili R, Raghunathan V S. Metall Mater Trans, 1999; 30A: 162

[17] Baek J W, Nam S W, Kong B O. Key Eng Mater, 2005; 297–300: 463

[18] Peng Z F, Cai L S, Dang Y Y, Zhao L, Peng F F, Yang Z G, Yan G Z, Chen S G, Zhou J, Zhou Y G. Mater Sci Forum, 2012; 706–709: 2450

[19] Peng Z F, Dang Y Y, Peng F F. Acta Metall Sin, 2012; 48: 450

(彭志方, 党莹樱, 彭芳芳. 金属学报, 2012; 48: 450)

[20] Peng Z F, Cai L S, Peng F F, Hu Y P, Chen F Y. Acta Metall Sin, 2010; 46: 429

(彭志方, 蔡黎胜, 彭芳芳, 胡永平, 陈方玉. 金属学报, 2010; 46: 429)

[21] Peng Z F, Peng F F, Chen F Y. Electr Power Constr, 2009; 30(12): 1

(彭志方, 彭芳芳, 陈方玉. 电力建设, 2009; 30(12): 1)

[22] Peng F F, Peng Z F, Chen F Y. In: Chinese Society for Electrical Engineering ed., Symposium on Localization of A New Steel For 600 MW/1000 MW Ultra–Supercritical Units, Zibo: EPTCINA.CN, 2009: 178

(彭芳芳, 彭志方, 陈方玉. 见: 中国电机工程学会主编, 600 MW/1000 MW超超临界机组新型钢国产化研讨会报告文集, 淄博: 中国电力科技网, 2009: 178)

文章导航

/