通过腐蚀失重、电化学测试、锈层分析和微观形貌观察研究了海水压力对不同成分2种低合金钢(X和Y)腐蚀行为的影响. 结果表明, X钢更易受到海水压力的影响而被加速腐蚀.深海压力均加速了2种低合金钢的阳极溶解速度; 压力对于X钢的氧扩散还原过程影响很小,而海水压力的增加导致Y钢阴极电流密度降低的原因是腐蚀产物直接参与了阴极还原反应.2种钢均由低压下的均匀腐蚀变为高压下的局部腐蚀, 但腐蚀形貌有较大差异.高压下的X钢表面出现明显的“浅碟状”腐蚀坑, 而高压下的Y钢表面出现了明显的隧道形腐蚀坑.
In this paper, the effect of hydrostatic pressure on the corrosion behaviors of two steels was investigated by weight loss test, electrochemical measurements, rust layer analysis and morphology observation in natural seawater environment with high–pressure in lab. The results showed that X steel was inclined to being corroded. With the increase of hydrostatic pressure, the corrosion resistance of two steels were deteriorated, which were attributable to the increase of the anodic reaction rate. Hydrostatic pressure had little effect on oxygen diffusion reductin process of X steel. Howeve, the cathodic current density of Y steel under higher hydrostatic pressure decreased because the coosion products were directly involved in cathodic reduction reaction. And with the increase of hydrostatic pressure, the morphology of two steels changed significantly and dfferently. Under high pressure, some shallo–dish shape localized corrosion appeared on the surface of X steel whereas on the surface of Y steel some tunnel localized crrsion appeared.
[1] Wang J, Meng J, Tang X, Zhang W. J Chin Soc Corros Prot, 2007; 27: 1
(王佳, 孟洁, 唐晓, 张伟. 中国腐蚀与防护学报, 2007; 27: 1)
[2] Guo W M, Li W J. Equip Enviro Eng, 2006; 3: 60
(郭为民, 李文军. 装备环境工程, 2006; 3: 60)
[3] Xu L K, Li W J, Chen G Z. Mari Sci, 2005; 29: 1
(许立坤, 李文军, 陈光章. 海洋科学, 2005; 29: 1)
[4] Guo W M, Li W J, Chen G Z. Equip Enviro Eng, 2006; 3: 10
(郭为民, 李文军, 陈光章. 装备环境工程, 2006; 3: 10)
[5] Schumacher M. Seawater Corrosion Handbook, New Jersey: Noyes Data Corporation, 1979: 107
[6] Dexter S. Corrosion, 1980; 36: 423
[7] Sawant S, Wagh A. Corros Prevent Contr, 1990; 37: 154
[8] Venkatesan R, Venkatasamy M, Bhaskaran T, Dwarakadasa E. Br Corros, 2002; 37: 257
[9] Chen S, Hartt W, Wolfson S. Corrosion, 2003; 59: 721
[10] Beccaria A M, Poggi G, Castello G. Br Corros, 1986;21: 19
[11] Beccaria A M, Poggi G, Gingaud D, Castello P. Br Corros,1994; 29: 65
[12] Beccaria A M, Poggi G, Arfelli M, Mattongno D. Corros Sci, 1993; 34: 989
[13] Chen S, Hartt W. Corrosion, 2002; 58: 38
[14] Beccaria A M, Poggi G, Gingaud D, Castello G. Br Corros, 1995; 30: 283
[15] Liu B, Cong Y, Zhang T, Shao Y W, Meng G Z,Wang F H. Corros Sci Prot Technol, 2009; 21: 5
(刘斌, 丛园, 张涛, 邵亚薇, 孟国哲, 王福会. 腐蚀科学与防护技术, 2009; 21: 5)
[16] Zhang T, Yang Y G, Shao Y W. Electrochim Acta, 2009; 15: 3915
[17] Yang Y G, Zhang T, Shao Y W, Meng G Z, Wang F H. Corros Sci, 2010; 52: 2697
[18] Practice for Laboratory Immersion Corrosion Testing of Metals, ASTM Standard G31, 1999
[19] Raman A, Kuban B, Razvan A. Corros Sci, 1991; 31: 1295
[20] Dunnwald J, Otto A. Corros Sci, 1989; 29: 1167
[21] Hu T, Lu X, Yan Y, Fu Y Y, Zhang H, Zhang S L. Spectrosc Spectr Anal, 2004; 24: 1072
(胡涛, 路欣, 阎研, 傅云义, 张 酣, 张树霖. 光谱学与光谱分析, 2004; 24: 1072)
[22] Xiao H, Wang S, Huang Z Z, Lin D Y. J Univ Sci Technol Beijing, 1997; 9: 476
(肖珩, 汪崧, 黄震中, 林定一. 北京科技大学学报, 1997; 9: 476)
[23] Li Y T, Li T X, Hou B R, Zhang J L. Oceanol Limnol Sin, 1998; 29: 651
(李言涛, 李延旭, 侯保荣, 张经磊. 海洋与湖沼, 1998; 29: 651)
[24] Antony H, Perrin S, Dillmann Ph, Legrand L, Chauss´e A. Electrochim Acta, 2007; 52: 7754
[25] Stratmann M, M¨uller J. Corros Sci, 1994; 36: 327
[26] Stratmann M, Hoffmann K. Corros Sci, 1989; 29: 1329
[27] Stratmann M, Streckel H. Corros Sci, 1990; 30: 697