间接超声振动制备5052铝合金半固态浆料 |
吕书林, 吴树森, 戴维, 安萍, 毛有武 |
华中科技大学材料成形与模具技术国家重点实验室, 武汉 430074 |
|
PREPARATION OF SEMISOLID 5052 ALUMINUM ALLOY SLURRY BY INDIRECT ULTRASONIC VIBRATION |
LU Shulin, WU Shusen, DAI Wei, AN Ping, MAO Youwu |
State Key Lab of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074 |
引用本文:
吕书林 吴树森 戴维 安萍 毛有武. 间接超声振动制备5052铝合金半固态浆料[J]. 金属学报, 2011, 47(5): 634-640.
,
,
,
,
.
PREPARATION OF SEMISOLID 5052 ALUMINUM ALLOY SLURRY BY INDIRECT ULTRASONIC VIBRATION[J]. Acta Metall Sin, 2011, 47(5): 634-640.
[1] Wu S S, Zhao J W, Zhang L P, An P, Mao Y W. Solid State Phenom, 2008; 141–143: 451
[2] Zhao JW,Wu S S, Wan L, Chen Q H, An P. Acta Metall Sin, 2009; 45: 314
(赵君文, 吴树森, 万里, 陈启华, 安 萍. 金属学报, 2009; 45: 314)
[3] Zhao JW,Wu S S, An P, Mao YW. Solid State Phenom, 2008; 141–143: 767
[4] Abramov V, Abramov O, Bulgakov V, Sommer F. Mater Lett, 1998; 37: 27
[5] Eskin G I, Eskin D G. Ultrason Sonochem, 2003; 10: 297
[6] Jian X, Xu H, Meek T T, Han Q. Mater Lett, 2005; 59: 190
[7] Gao D M, Li Z J, Han Q Y, Zhai Q J. Mater Sci Eng, 2009; A502: 2
[8] Liu Q M, Zhang Y, Song Y L, Qi F P, Zhai Q J. Mater Des, 2007; 28: 1949
[9] Kaibyshev R, Musin F, Lesuer D R, Nieh T G. Mater Sci Eng, 2003; A342: 169
[10] Piao L, Motegi T. J Jpn Inst Light Met, 2005; 55(2): 86
[11] Lu S L, Wu S S, Zhu Z M, An P, Mao Y W. Trans Nonferrous Met Soc China, 2010; 20: 758
[12] Lu S L, Wu S S, Dai W, Zhu Z M, Mao, Y W, Wan L. Spec Cast Nonferrous Alloys, 2010; 30: 326
(吕书林, 吴树森, 戴维, 朱泽明, 毛有武, 万 里. 特种铸造及有色合金, 2010; 30: 326)
[13] Liu C, Pan Y, Aoyama S. In: Bhasin A K, Moore J J, Young K P, Midson S, eds., Proc 5th Int Conf on Semi–solid Processing of Alloys and Composites, Colorado: Golden, 1998: 431
[14] Kapustina O A. The Physical Principles of Ultrasonic Manufactureing. Moscow: Nauka, 1970: 45
[15] Ohno A. Solidification: The Separation Theory and Its Practical Applications. Berlin: Springer, 1987: 1
[16] Qian M, Ramirez A, Das A. J Cryst Growth, 2009; 311: 3708
[17] Wu S S, Xie L Z, Zhao J W, Nakae H. Scr Mater, 2008; 58: 556
[18] Qian M, Ramirez A, Das A, Stjohn D H. J Cryst Growth, 2010; 312: 2267
[19] Taghavi F, Saghafian H, Kharrazi Y H K. Mater Des, 2009; 30: 115
[20] Campbell J. Int Mater Rev, 1981; 2: 71 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|