金属学报  1959, Vol. 4 Issue (3): 262-269

论文 本期目录 | 过刊浏览 |

石氏体的回火脆性

谭玉华

鞍山钢铁工业学院

THE TEMPER-BRITTLENESS OF BAINITIC STEELS

TAN YU-HUA Anshan Institute of Iron and Steel Technology

谭玉华. 石氏体的回火脆性[J]. 金属学报, 1959, 4(3): 262-269.
. THE TEMPER-BRITTLENESS OF BAINITIC STEELS[J]. Acta Metall Sin, 1959, 4(3): 262-269.

摘要 参考文献 相关文章 Metrics 全文: PDF(715 KB)   摘要: 本文系统地研究了在石氏体组织中所发生的回火脆性。下石氏体在回火过程中脆化的趋势略小于回火马氏体,上石氏体的脆化趋势略大于珠光体,而回火马氏体的回火过程的脆化趋势远大于珠光体。上石氏体的回火脆性发生温度区域是460—580℃,回火马氏体是430—630℃,两者的最大回火脆性温度都是530℃。 Abstract：A study of the occurrence of temper-brittleness in bainitic structure has been made. It wasfound that the tendency of temper-embrittlement in the lower bainite was slightly less than thatin the tempered martensite whik the temper-embrittlement in the upper bainite was slightly greaterthan that in pearlitic structure, and the tendency of temper embrittlement of the temperedmartensite was much greater than that of the pearlite. The temperature range of temper-brittleness was 460—580℃ for upper bainite, 430—620℃ for tempered martensite, and the tem-perature of maximum temper-embrittlement appeared to be about 530℃ for both. It was sug-gested that the mechanism of temper-brittleness is the same for both structures. 收稿日期: 1959-03-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 谭玉华 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1959/V4/I3/262 [1] R. H. Grenves and J. A. Jones: J. Iron Steol Inst., 1920, 102, 171． [2] Н. Н. Минкевич: ЖРМО, 1927, № 1, 52． [3] E. Mnurer, O. H. Wilms und H. Kiassler: Stahl und Eisen, 1942, 62, 81． [4] W. S. Pellini and B. R. Queneau: Trans. A. S. M., 1947, 39, 139． [5] B. C. Woodfine: J. Iron Steel Inst., 1953, 173, 229． [6] N. P. Allen and C. C. Eanley: ibid., 1956, 182, 375． [7] Т. В. Сергиевская: Сталь, 1955, № 1, 63． [8] D. C. Buffum and L. D. Jaffe: Trans. A. I. M. E., 1953, 197, 1373． [9] Atlas of Isothermal Transformation Diagrams, 19． [10] Н. Т. Гулцова, М. Л. Бернщтейна, А. Г. Ражштадта: 1956, 436． [11] Л. В. Смирнов, Д. Д. Садовский: 1956． [12] В. А. 捷列:合金构钢,重工业出版社,1956． [13] С. Т. Кишкин: 1941, № 4, 91． [14] Л. С. Ольховой и Д. Я. Вишняко: 1956, 36． [15] D. McLean and L. Northcott. J. Iron Steel Inst., 1948, 158, 169． [16] В. И. Архаров: 1946, 8; 1955, 16． [17] R. Maloof: Trans. A. S. M., 1952, 44, 264; 或 1953, № 3, 121． [18] Н. В. Казакова, Н. В. Королева: 1955, 105, № 6, 1233． [19] С. Ф. Юрьев: 1956, № 10, 37． [20] H. A. Dichie: Stahl und Eisen, 1928, 48, 50． [21] Honda Katar: Metal Ptogress, 1933, (6) , 43． [22] А. Н. Ризоль, Л. Г. Сакварелдзе и Л. М. Утевский: 1955, 105, 268． [23] 雄井英雄:日本金属学会会志,1956(10) ,20,550． [24] А. С. Завьяков, Л. Я. Гольдштейн и М. И. Сенченко: 1957． [25] J. H. S. Dickensan: J. West. Scotland, Iron Stoel Inst., 1919, 110．b No related articles found! Viewed Full text Abstract Cited   Shared      Discussed