金属学报  1965, Vol. 8 Issue (3): 352-424

论文 本期目录 | 过刊浏览 |

铁-锰-铝系复相铜中的β_(Mn)型相变

张彦生;王处义;师昌绪

THE FORMATION OF A β_Mn. TYPE PHASE IN SOME Fe-Mn-Al STEELS

CHANG YEN-SHEN;WANG CHU-YI;SHIH CHANG-HSU

张彦生;王处义;师昌绪. 铁-锰-铝系复相铜中的β_(Mn)型相变[J]. 金属学报, 1965, 8(3): 352-424.
, , . THE FORMATION OF A β_Mn. TYPE PHASE IN SOME Fe-Mn-Al STEELS[J]. Acta Metall Sin, 1965, 8(3): 352-424.

摘要 参考文献 相关文章 Metrics 全文: PDF(3961 KB)   摘要: 报道了以金相观察、X射线衍射、显微硬度、硬度、冲击试验等方法所研究的几个Fe-Mn-Al复相(δ+γ)钢(33—37％Mn,5—9％Al的基体)中的β_Mn型相交的试验结果。测定了βMn型相变的温度范围,观察了自δ铁素体及奥氏体中分解出βMn相的过程。并讨论了成分、热处理条件的影响。 Abstract：The formation of β_(Mn) type structure in several Fe-Mn-Al duplex steels with com-positions varying from 33 to 37％ Mn and 5 to 9％ Al has been systematically stud-ied by microscopic examination, X-ray diffraction analysis, microhardness indentation test,hardness measurement and impact test. The temperature range of transformation for (δ+γ) to β_(Mn) lies between 500°and1000℃. The lower temperature limit is lowered by the addition of Al and the upperlimit raised by Mn and Al. The morphology of β_(Mn) formed depends on the composition and heat treatment ofthe alloys. β_(Mn) needles are preferentially originated from δ/δ and δ/γ grain boundaries,ferrite grains, etc., and then grow into rods. At higher temperatures β_(Mn) forms inblocks along the δ/γ boundaries and later grows into δ-ferrite grains. A relief effect onthe polished surface has been observed after the formation of β_(Mn) needles and it is sug-gested that this β_(Mn) is formed by the bainitic transformation mechanism. It has beenfound that the impact value decreases and the hardness increases with increasing β_(Mn)content. 收稿日期: 1965-03-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 张彦生 王处义 师昌绪 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1965/V8/I3/352 [1] Koster, W., Tonn, W.: Arch. Eisenhuttenw., 1933-34, 7, 365． [2] Schmatz, D. T.: Trans. AIME, 1959, 215． 113． [3] 张彦生、师昌绪:金属学报,1964,7,285． [4] 张彦生、师昌绪、李有柯:金属学报,1965,8,346． [5] Hansen, M., Anderk, A.: Constitution of Binary Alloys, 2nd ed., (McGraw-Hill, 1958) , p. 111, 665, 954． [6] Bradley, A. J., Jones, P.: Phil. Mag., 1931, 12, 1137． No related articles found! Viewed Full text Abstract Cited   Shared      Discussed