准解理断裂的本质

廖乾初;孙福玉;蓝芬兰

北京钢铁研究院;北京钢铁研究院;北京钢铁研究院

AN INVESTIGATION OF QUASI-CLEAVAGE FRACTURE IN STEEL

Liao Chienchu;Sun Fuyu;Lan Fenlan Beijing Institute of Iron and Steel Research

引用本文:

廖乾初;孙福玉;蓝芬兰. 准解理断裂的本质[J]. 金属学报, 1979, 15(2): 259-313.
, , . AN INVESTIGATION OF QUASI-CLEAVAGE FRACTURE IN STEEL[J]. Acta Metall Sin, 1979, 15(2): 259-313.

全文: PDF(2436 KB)

摘要: 本文试图探讨准解理断裂的本质。联系多晶材料的典型应力一应变曲线,对不同钢的断裂韧度试样的断口分析表明,准解理断裂可以看作是一种过渡的断裂机制。首先,一系列微观解理裂纹在高拉伸应力集中地方生核,然后这些裂纹各自沿着它本身已变形晶粒的解理面上扩展,最后借助于微观塑性聚合方式,这些微裂纹彼此连接。根据上述断裂模型可以认为:解理裂纹与塑性变形间的相互作用是准解理断裂的一种重要性质。借助于断口定量分析方法,有可能把断口形貌和一些力学参数间关系建立起来。

Abstract：The quasi-cleavage fracture has been studied in conjunction with the stressstrain behaviour of steel specimens. Consideration of the results obtained on dif-ferent varieties of steel indicate that the quasi-cleavage fracture may be interpretedin terms of certain transition fracture mechanism as follows: Microcleavage cracks are nucleated at certain places of high tensile strss con-centration, subsequently each of them propagates along the cleavage plane in grainsalready deformed and finally they merge together by microplastic coalescence.According to the above conception, the interaction between the cleavage crack andthe plastic deformation may be regarded as the most important characteristics ofquasi-cleavage fractures. Using quantitative fractography, correlation between thefractographic features of specimens and the parameters of its certain mechanicalproperties may be established.

收稿日期: 1979-02-18

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	廖乾初
	孙福玉
	蓝芬兰
44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y1979/V15/I2/259

[1] Beachem, C. D. and Relloux, R. N., Amer. Soc. Test. Mater., Spec. Tech. Publ. № 381, ASTM, 1964, p. 210．
[2] Sullivan, C. P., Weld. Res. Counc. Bull., (1967) , May, 122．
[3] Thomas, K. S., Klingcle, H. and Woitscheck, A., Pract. Metallogr., 11 (1970) , № 10, 538．
[4] Matsuda, S., Trans. Jap. Inst. Metals, 11 (1970) , 371．
[5] Terasaki, T., Trans. Iron Steel Inst. Jap., 12 (1972) , 45．
[6] Beachem, C. D., Met. Trans., 4 (1973) , 1999．
[7] Evans, P. K. V.. J. Iron Steel Inst., London, 210 (1972) . 200．
[8] 北京钢铁研究院,工程断裂力学,上册,国防工业出版社,1977年,p.106．
[9] 饭田国广,金属材料,12(1972) ,№ 3,85．
[10] 北京钢铁研究院,长时运行的12CrlMoV主蒸汽管试验总结,1977年.
[11] 廖乾初, 未发表工作.
[12] 陈箎,私人通讯.

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed