从相图剖析炉外精炼渣对MgO-CaO系材料的侵蚀

陈肇友

冶金工业部洛阳耐火材料研究所

DISCUSSION ON OFF-FURNACE STEEL REFINING SLAG ATTACK UPON MgO-CaO REFRACTORIES FROM ASPECT OF CaO-SiO_2-Al_2O_3-MgO QUARTERNARY PHASE DIAGRAM

CHEN Zhaoyou (Luoyang Institute of Refractory Research; Ministry of Metallurgical Industry)

陈肇友. 从相图剖析炉外精炼渣对MgO-CaO系材料的侵蚀[J]. 金属学报, 1983, 19(6): 79-85.
. DISCUSSION ON OFF-FURNACE STEEL REFINING SLAG ATTACK UPON MgO-CaO REFRACTORIES FROM ASPECT OF CaO-SiO_2-Al_2O_3-MgO QUARTERNARY PHASE DIAGRAM[J]. Acta Metall Sin, 1983, 19(6): 79-85.

摘要 参考文献 相关文章 Metrics 全文: PDF(553 KB)   摘要: 本文根据有关三元系相图绘制出CaO-SiO_2-Al_2O_3-MgO四元系于1600℃时的液相区、饱和面。通过计算还绘出1600℃时MgO在CaO-SiO_2-Al_2O_3渣中的溶解度图,以及MgO-CaO系材料在高温时同时吸收一定量Al_2O_3与SiO_2后产生的液相量。 依据这些图,分析讨论了炉外精炼渣对MgO-CaO系材料的侵蚀。从控制炉渣成分和选择恰当的MgO-CaO材料组成两个方面提出了改善炉衬寿命的途径。 Abstract：From the aspect of the phase diagram, the slags of the off-furnace steel refinement may be substantially considered similar in nature of a CaO-SiO_2-Al_2O_3-MgO quarternary system. The liquid zone and the saturation surface at 1600℃ of this system and the MgO solubility line at 1600℃ in CaO-SiO_2-Al_2O_3 slags as well as the quantity of liquid formed in different compositions of MgO-CaO system refractories after absorbed a certain amount of SiO_2 and Al_2O_3 at 1700℃ have been constructed by the allied ternary phase diagrams and the published data. Based upon above-mentioned, the off-furnace steel refining slags attack upon the MgO-CaO system refractories was discussed. Suggestion may be made of the improvements upon the service life of the linings either by controlling the composition of slags or by selecting properly the constituents of MgO-CaO refractories. 收稿日期: 1983-06-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 陈肇友 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1983/V19/I6/79 1 Kaufman, J. W.; Aguirre, C. E., Electr. Furnace Proc., 35 (1977) , 74． 2 Levin, E. M.; Robbins, C. R.; McMurdie, H. F., Phase Diagrams for Ceramists, 2nd ed., Am. Ceram. Soc., 1969, p. 210, 219, 246． 3 Muan, A,; Osborn, E. F., Phase Equilibria Amang Oxides in Steelmaking, Addison-Wesley, Reading, Massachusetts, 1965, p. 101, 130-136． 4 Herzog, S. P., Scand. J. Metall., 5 (1976) , 145． 5 O'hara, M. J.; Biggar, G. M., Trans. Br. Ceram. Soc., 69 (1970) , 243． 6 Levin, E. M.; McMurdie, H. F., Phase Diagrams for Ceramists 1975 Supplement, Ed. Reser, M. K., Am. Ceram. Soc., Columbus, Ohio, p. 267-276 7 山本力;田中征二郎;佐佐木三明,耐火物,33 (1981) ,216． 8 Sata, T.; Sasamoto, T.; Lee, H-L., Rep. Res. Lab. Eng. Mater., Tokyo Inst, Technol., 3 (1978) , 41． 9 高宫陽一;长谷川安利;田贺井秀夫;岚治夫,耐火物,27(1975) ,242． No related articles found! Viewed Full text Abstract Cited   Shared      Discussed