金属学报  1994, Vol. 30 Issue (11): 491-501

论文 本期目录 | 过刊浏览 |

贝氏体相变的激发-台阶机制

方鸿生;王家军

清华大学;北京电子显微镜实验开放研究基金

SYMPATHETIC-LEDGEWISE MECHANISM OF BAINITIC TRANSFORMATION

FANG Hongsheng;WANG Jiajun(Tsinghua University; Beijing)(Manuscript received 20 July; 1994)

方鸿生;王家军. 贝氏体相变的激发-台阶机制[J]. 金属学报, 1994, 30(11): 491-501.
, . SYMPATHETIC-LEDGEWISE MECHANISM OF BAINITIC TRANSFORMATION[J]. Acta Metall Sin, 1994, 30(11): 491-501.

摘要 参考文献 相关文章 Metrics 全文: PDF(891 KB)   摘要: 简要总结了贝氏体相变切变及扩散控制台阶长大理论面临的主要问题．并首次基于台阶长大理论，提出贝氏体相变的激发－台阶机制及其相变模型． 关键词 ： 贝氏体相变,  相变机制,  相变模型,  激发－台阶机制     Abstract：The main problems encountered by shear and diffusion controlled ledgewise mechanisms of bainitic transformation have been reviewed. Based on the ledgewise growth theory, a sympathetic-ledgewise mechanism and its transformation model describing bainitic formation in both steels and non-ferrous alloys have been presented. Correspondent: WANG Jiajun,Depantment of Materials Science, Tsinghua Univesity, Beijing 100084） Key words： bainitic transformation    transformation mechanism    transformation model    sympathetic-ledgewise mechanism 收稿日期: 1994-11-18      基金资助:国家自然科学基金 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 方鸿生 王家军 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1994/V30/I11/491 1HehemannRF,KinsmanKR,AaronsonHI．MetallTrans,1972;3A:10772AaronsonH I,ReynoldsWTJr,ShifletGJ,SpanosG．MetallTrans,1990;21A:13433SpeichGR．In:ZackayVF,AaronsonHIeds．,DecompositionAustenitebyDiffusionalProcesses,NY:IntersclencePublishers,1962:3534BhadeshiaHKDH,WaughAR,ActaMetall,1982;30:7755UnikrishnanM．J MaterSci,1978;13:14016 ClarkHM,WaymanCM,In:AaronsonHIed．,PhaseTransformations．MetalsPark,OH:ASM1970:597 SrinivasanGR,WaymanCM．ActaMetall,1968,16:6098WastonJD,McDougallPG．ActaMetall,1973;21:9619AaronsonHI．In:ZackayVF,AaronsonHIeds．,DecompositionAustenitebyDiffusionalPro-cesses,NY:IntersciencePublishers,1962:38710 Bhadeshia H KDH,EdmondsDV．ActaMetall,1980;28:110311 BhbadeshiaHKDH,ChristianJW．MetallTrans．1990;21A:76712FangHS,WangJJ,ZhengYK．MetallTrans,1994;25A,inpublishing13FangHS,WangJJ,ZhengYK,In:TamuraIed．,Heat&Surfac’92,Tokyol:JpnTechInformServPubl,1992:57914方鸿生,王家军,郑燕康,杨志刚．金属学报,1993;29:A44515OblackJM,HehemannRF．Tronsformations&HardenabilityinSteels,AnnArbor,MI:ClimaxMolybdenumCompany,1967:1516HehemannRF．In:AaronsonHIed．,PhaseTronsformations,MetalsPark,OH,ASM,1970:39717PickeringFB．Transformations&HardenabilityinSteels,AnnArbor,MI:ClimaxMolybdenumCompany,1967:10918ChristianJW．In:ZackayVF,AaronsonHIeds．,DecompositionAusteniteby DiffusionalPuocesses,NY:IntersciencePublishers,1962:37119ChristianJW．TheMechanismofPhaseTransformationsinCrystallineSolids,London:InstMetalls,1969:12920EichenE,AaronsonHI,PoundGM,TrivediR．ActaMetall,1964;12:129821方鸿生,李春明,王家军．金属学报,1993;29:A38322方鸿生,白秉哲．金属学报,1986;22:A28323HabrakenLJ,EconomopoulosM．Transformations&HardenabilityinSteels．AnnArbor,MI:ClimaxMolybdenumCompany,1967:6924NilanTG．Transformations&HardenabilityinSteels, Ann Arbor,MI:ClimaxMolybdenumCom-pany,1967:5725KinsmanKR,AaronsonHI．MetallTrans,1970;1A:148526FangHS,WangJJ,LiCM．PacificRimConferenceontheRolesofShear&DiffusionintheFor-mationofPlate-ShapedTransformationProducts,Hawaii,USA:1992;1527ChristianJW,EdmondsDV．PhaseTransformations．inFerrousalloy,Warrendale,PA:TMS,1984;29328王家军,清华大学博士学位论文,199329王家军,方鸿生,杨志刚,李春明．金属热处理学报,1994;15(2):1330方鸿生,王家军,杨志刚,李春明,邓旭蕊,郑燕康．自然科学进展,1993:3:52531AaronsonHI,WellC．TransAIME,1956;206:121632WangJJ,FangHS,YangZG,ZhengYK．MaterChar,1994,inpublishing33王家军,方鸿生,郑燕康,严隽珏．兵器材料科学与工程,1993;16(4):334严隽珏,方鸿生,王家军．科学通报,1994,39:11435FangHS,WangJJ,ZhengYK．Heat&Surface’94,France,Seine,199436StreetJA,JInstMetals,1959;88:38137 MenonESK,AaronsonHI．AclaMetall,1987;35:549? [1] 王长军，孙新军，雍岐龙，李昭,张熹，江陆. 贝氏体相变温度对含Ti和Mo低碳热轧TRIP钢的组织与力学性能影响及析出相的微观结构表征[J]. 金属学报, 2013, 29(4): 399-407. [2] 康沫狂 张明星 刘峰 朱明. 金属合金等温相变的体激活能及相变机制 I. 钢的中温(贝氏体)等温相变[J]. 金属学报, 2009, 45(1): 25-31. [3] 方鸿生; 冯春; 郑燕康; 郑秀华; 张弛; 白秉哲 . 下贝氏体中碳化物的析出[J]. 金属学报, 2007, 43(6): 583-588 . [4] 王振清; 周博; 梁文彦 . 形状记忆合金的本构关系[J]. 金属学报, 2007, 43(11): 1211-1220 . [5] 方鸿生; 杨志刚; 杨金波; 白秉哲 . 钢中贝氏体相变机制的研究[J]. 金属学报, 2005, 41(5): 449-457 . [6] 于少飞; 钱百年; 国旭明 . ULCB熔敷金属组织与碳、氧含量对力学性能的影响[J]. 金属学报, 2005, 41(10): 1082-1086 . [7] 徐祖耀 . 应力对钢中贝氏体相变的影响[J]. 金属学报, 2004, 40(2): 113-119 . [8] 刘晓; 钟凡 . 贝氏体相变理论——两个一级相变耦合的模型[J]. 金属学报, 1999, 35(11): 1135-1138 . [9] J.W.Christian. 相变中的界面(英文)[J]. 金属学报, 1997, 33(2): 150-156. [10] 方鸿生;杨志刚;王家军;郑燕康. 贝氏体和马氏体相变及应用的研究[J]. 金属学报, 1996, 32(4): 337-350. [11] 方鸿生;李春明;王家军. Cu-Zn-Al合金贝氏体的初生态及三维台阶[J]. 金属学报, 1993, 29(9): 1-5. [12] 孟祥康;康沫狂. Cr-Zn-Al合金溶质原子贫化区贝氏体切变形核的原位观察[J]. 金属学报, 1993, 29(8): 25-30. [13] 徐祖耀;周晓望. Cu-Al合金贝氏体相变热力学[J]. 金属学报, 1992, 28(6): 26-28. [14] 孙加林;康沫狂. 下贝氏体亚结构及晶体学分析[J]. 金属学报, 1991, 27(3): 72-76. Viewed Full text Abstract Cited   Shared      Discussed