PROPOSAL OF STRUCTURE FORMATIONIN SELFPROPAGATING HIGH TEMPERATURE SYNTHESIS OF TiB_2-xAl COMPOSITES
FU Zhengyi;WANG Weimin;WANG Hao;YUAN Runzhang(Wuhan University of Technology);MUNIR;Zuhair A.(University of California;Davis; USA)
引用本文:

傅正义;王为民;王浩;袁润章. TiB_2-xAl复合材料的结构形成分析[J]. 金属学报, 1994, 30(20): 373-378.
, , , . PROPOSAL OF STRUCTURE FORMATIONIN SELFPROPAGATING HIGH TEMPERATURE SYNTHESIS OF TiB_2-xAl COMPOSITES[J]. Acta Metall Sin, 1994, 30(20): 373-378.

全文: PDF(437 KB)  
摘要: 研究了Ti和B颗粒尺寸的变化对自蔓延高温合成(SHS)TiB_2—xAl金属基复合材料的燃烧温度和燃烧波速度的影响。结果表明,Al颗粒不直接参与化学反应,其尺寸变化对SHS过程的影响要小得多,但是反应过程中形成的熔融Al能阻止TiB_2晶粒的长大,因而可以控制SHS产物的结构。通过燃烧波峰淬熄(CFQ)法,对该复合材料的SHS过程结构形成机理进行了分析。
关键词 TiB_2—xAl复合材料结构形成分析自蔓延高温合成    
Abstract:Effect of of Ti or B particle size on the combustion temperature and propa gating rate in the self—propagating high temperature synthesis(SHS) process of TiB_2-xAl composites has been investigated.The size change of Al particles,which does not directly enter into the chemical reaction as Ti and B,may be much less influential to the SHS process.But the molten Al, formed during reaction, may retard the growth of TiB_2grains. Thus, the structure of SHS product can be controlled.By means of combustion front quenching (CFQ) with copper wedge, the structure formation of TiB_2-xAl composites in the SHS process was discussed
Key wordsTiB_2-xAl composite    structure formation    self—propagating high temperature synthesis
    
1傅正义,袁润章,MunirZA.金属学报,1993;29:B3342MerzhanovAG.PureApplChem,1992;64:9413RogachevAS,MukasyanAS,MerzhanovAGDoklAkadNaukSSSR,1987;297:14254FuZY,WangWM,WangH,YuanRZ.PACRIMMeetingProceed,Hawaii,USA,1993:1425YuanRZ,FuZY,YangZL,MunirZA.JMaterSynthProcess,1993;1:153
[1] 刘长松; 刘永合 . 火焰喷涂合成TiC—Fe涂层的热力学分析[J]. 金属学报, 2000, 36(1): 62-66 .
[2] 严新炎;张树格;孙国雄. Ni_3Si体系的螺旋燃烧[J]. 金属学报, 1995, 31(13): 15-20.
[3] 傅正义;袁润章;MunirZA. TiB_2-xAl复合体系的SHS合成过程研究[J]. 金属学报, 1993, 29(7): 92-96.