CaO-SiO_2-Al_2O_3-FeO熔渣起泡行为的研究

黄宗泽;肖兴国;肖泽强

东北大学

FOAMING BEHAVIOUR OF CaO-SiO_2-Al_2O_3-FeO SLAGS

HUANG Zongze; XIAO Xingguo; XIAO Zeqiang(Department of Ferrous Metallurgy; Northeastern University; Shenyang 110006); Singh S D(National Metallurgical Laboratory; Jamshedpur; India 831007)(Manuscript received 1994-04-26)

黄宗泽;肖兴国;肖泽强. CaO-SiO_2-Al_2O_3-FeO熔渣起泡行为的研究[J]. 金属学报, 1995, 31(19): 289-294.
, , . FOAMING BEHAVIOUR OF CaO-SiO_2-Al_2O_3-FeO SLAGS[J]. Acta Metall Sin, 1995, 31(19): 289-294.

摘要 参考文献 相关文章 Metrics 全文: PDF(378 KB)   摘要: 在１５００℃下，用Ｘ射线透视装置研究了ＣａＯ－ＳｉＯ_２－Ａｌ_２Ｏ_３－ＦｅＯ熔渣被石墨还原过程中渣的起泡行为，测定了熔渣的起泡指数和起泡率等参数．结果表明，随熔渣碱度上升，其起泡率增大而起泡指数却下降．同时考察了ＭｇＯ，ＣａＦ_２，Ｎａ_２Ｏ等添加物对熔渣起泡行为的影响．通过对熔渣起泡指数的因次分析得到，熔渣起泡指数与熔渣粘度，密度，表面张力及重力加速度ｇ有如下关系： 关键词 ： ＣａＯ－ＳｉＯ_２－Ａｌ_２Ｏ_３－ＦｅＯ熔渣,  起泡指数,  因次分析,  炼铁工艺     Abstract：The foaming behaviour of CaO-SiO_2-Al_2O_3-FeO slag system reduced by graphite at 1500℃ was quantitatively studied with the help of X-ray apparatus. Foaming parameters such as foaming ratio and foaming index were determined. It was found that with increase of the basicity of slags, the foaming ratio increased, however, the foaming index was opposite. In addition, the effects of additives like MgO, Na_2O and CaF_2 on the foaming behaviour were also investigated. The result of dimensional analysis showed that the foaming index(∑) of molten slag was determined by where μ is the viscosity of the slag,σis the surface tension, ρis the density of the slag and g is the acceleration of gravity. (Correspondent: HUANG Zongze, Department of Ferrous Metallurgy, Northeastern University, Shenyang110006) Key words： CaO-SiO_2-Al_2O_3-FeO slag    foaming index    dimensional analysis    smelting reduction      基金资助:国家自然科学基金 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 黄宗泽 肖兴国 肖泽强 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1995/V31/I19/289 1CooperCF,KitchenerJA．JIronSteelInst,1959;193(1):482原茂太,生田昌久,北村光章,荻野和巳．铁钢,1983;69(9):11523ItoK,FruehanRJ．MetallTrans,1989;20B(4):5094YoonJK．IntConfonNewSmeltingReductionandNearNetShapeCastingTechnforSteel,Pohang:TheKoreanInstMetals,1990:975OgawaY,KatayamaH,HirataH,TokumitsuN,YamauchiM．ISIJInt,1992;32(1):876JiangR,FruehanRJ．MetallTrans,1991;22B(4):4817黄宗泽,肖兴国,肖泽强．东北大学学报,1994;15(2):1408KeeneBJ,MillsKC．IntMaterRev,1987;32(1):1059GuthrieRIL．EngineeringinProcessMetallurgy,OxfordScienccPublications,1989:15110NakashimaK,MoriK．ISIJInt,1992;32(1):1111UrbainG．SteelRes,1987;58(3):111 [1] 黄宗泽;肖兴国;肖泽强. 含FeO熔渣的起泡过程及起泡参数间关系分析[J]. 金属学报, 1996, 32(3): 278-283. Viewed Full text Abstract Cited   Shared      Discussed