Mo含量对1000 MPa级高强钢焊缝金属组织和力学性能的影响
Effect of Mo Content on the Microstructure and Mechanical Properties of 1000 MPa Grade High-Strength Steel Weld Metal
(a) Mo00 (b) Mo03 (c) Mo07
Mo含量对1000 MPa级高强钢焊缝金属组织和力学性能的影响 |
| 刘洋, 孙健, 陆善平 |
|
Effect of Mo Content on the Microstructure and Mechanical Properties of 1000 MPa Grade High-Strength Steel Weld Metal |
| LIU Yang, SUN Jian, LU Shanping |
| 图13 不同Mo含量焊缝金属的室温冲击载荷-位移曲线 |
| Fig.13 Impact load-displacement curves of weld metal with different Mo contents at room temperature (Ei—crack initiation energy, Ep—crack propagation energy) (a) Mo00 (b) Mo03 (c) Mo07 |
|
|