Mo含量对1000 MPa级高强钢焊缝金属组织和力学性能的影响
Effect of Mo Content on the Microstructure and Mechanical Properties of 1000 MPa Grade High-Strength Steel Weld Metal
Mo含量对1000 MPa级高强钢焊缝金属组织和力学性能的影响 |
| 刘洋, 孙健, 陆善平 |
|
Effect of Mo Content on the Microstructure and Mechanical Properties of 1000 MPa Grade High-Strength Steel Weld Metal |
| LIU Yang, SUN Jian, LU Shanping |
| 图9 Mo00焊缝金属中残余奥氏体的TEM明场像、暗场像及SAED花样 |
| Fig.9 TEM bright field (a) and dark field (b) images and corresponding SAED pattern (inset) of RA in Mo00 weld metal |
|
|