Mo含量对1000 MPa级高强钢焊缝金属组织和力学性能的影响
Effect of Mo Content on the Microstructure and Mechanical Properties of 1000 MPa Grade High-Strength Steel Weld Metal
(a, d) Mo00 (b, e) Mo03 (c, f) Mo07
Mo含量对1000 MPa级高强钢焊缝金属组织和力学性能的影响 |
| 刘洋, 孙健, 陆善平 |
|
Effect of Mo Content on the Microstructure and Mechanical Properties of 1000 MPa Grade High-Strength Steel Weld Metal |
| LIU Yang, SUN Jian, LU Shanping |
| 图8 不同Mo含量焊缝金属的反极图和相图 |
| Fig.8 Inverse pole figures (a-c) and phase maps (d-f) of weld metals with different Mo contents (RA—retained austenite) (a, d) Mo00 (b, e) Mo03 (c, f) Mo07 |
|
|