Mo含量对1000 MPa级高强钢焊缝金属组织和力学性能的影响
Effect of Mo Content on the Microstructure and Mechanical Properties of 1000 MPa Grade High-Strength Steel Weld Metal
Mo含量对1000 MPa级高强钢焊缝金属组织和力学性能的影响 |
| 刘洋, 孙健, 陆善平 |
|
Effect of Mo Content on the Microstructure and Mechanical Properties of 1000 MPa Grade High-Strength Steel Weld Metal |
| LIU Yang, SUN Jian, LU Shanping |
| 图2 不同Mo含量焊缝金属微观组织的OM像和SEM像 |
| Fig.2 OM (a-c) and SEM (d-f) images of weld metals with different Mo contents (CB—coalesced bainite, LB—lath bainite, PAGB—prior austenite grain boundary) (a, d) Mo00 (b, e) Mo03 (c, f) Mo07 |
|
|