直接退火与冷轧+退火处理Cu-Ni-Si/1010钢双金属复合材料的组织演变及强化机制

王明飞, 陶美悦, 宫臣, 彭博, 李廷举, 接金川

Microstructural Evolution and Strengthening Mechanisms of Cu-Ni-Si/1010 Steel Bimetallic Composites via Direct Annealing and Cold Rolling + Annealing

WANG Mingfei, TAO Meiyue, GONG Chen, PENG Bo, LI Tingju, JIE Jinchuan

图4 S1~S4样品界面附近Cu-Ni-Si合金侧和1010钢侧的反极图及对应的晶粒尺寸分布图

Fig.4 EBSD analysis results of samples S1-S4 near the interface (a1-d1) inverse pole figures (IPFs) of Cu-Ni-Si side in samples S1 (a1), S2 (b1), S3 (c1), and S4 (d1) (a2-d2) grain size distribution histograms corresponding to Figs.4a1-d1, respectively (a3-d3) IPFs of 1010 steel side in samples S1 (a3), S2 (b3), S3 (c3), and S4 (d3) (a4-d4) grain size distribution histograms corresponding to Figs.4a3-d3, respectively