低碳钢预制涡流搅拌摩擦焊工艺研究
Process of Prefabricated Vortex Flow-Based Friction Stir Welding for Low Carbon Steel
(a) 500 r/min, 20 mm/min, 0° (b, e) 500 r/min, 20 mm/min, 1° (c, f) 700 r/min, 20 mm/min, 1° (d) 300 r/min, 20 mm/min, 1°
低碳钢预制涡流搅拌摩擦焊工艺研究 |
| 王启勇, 李晓博, 刘小超, 王心成, 张泰瑞, 倪中华, 陈彪 |
|
Process of Prefabricated Vortex Flow-Based Friction Stir Welding for Low Carbon Steel |
| WANG Qiyong, LI Xiaobo, LIU Xiaochao, WANG Xincheng, ZHANG Tairui, NI Zhonghua, CHEN Biao |
| 图8 使用W-Re套筒在不同工艺参数下所获接头截面的OM像 |
| Fig.8 Cross-sectional low (a-d) and locally high (e, f) magnified OM images of joints obtained using W-Re holder under different parameters (a) 500 r/min, 20 mm/min, 0° (b, e) 500 r/min, 20 mm/min, 1° (c, f) 700 r/min, 20 mm/min, 1° (d) 300 r/min, 20 mm/min, 1° |
|
|