超声冲击制备梯度纳米结构Zr-4合金低温扩散连接界面组织与力学性能

杨旭, 杨振文, 王颖, 李会军, 李永兵

Interfacial Microstructure and Mechanical Properties of Low-Temperature Diffusion-Bonded Zr-4 Alloy with Gradient Nanostructure via Ultrasonic Impact Treatment

YANG Xu, YANG Zhenwen, WANG Ying, LI Huijun, LI Yongbing

表1 不同扩散连接温度下GNS-Zr/GNS-Zr接头的化学成分及相组成 (atomic fraction / %)

Table 1 Chemical compositions and possible phases of each point marked in Figs.6d-f

Point Zr Fe Cr Sn Possible phase 1 96.30 1.17 0.72 1.81 α-Zr 2 59.99 27.40 11.73 0.88 Eutectic α-Zr + Zr(Fe, Cr)2 3 52.60 35.19 11.05 1.16 Eutectic α-Zr + Zr(Fe, Cr)2 4 41.59 31.82 25.66 0.93 Zr(Fe, Cr)2