Mo含量对CrAlMoN涂层微观结构、力学性能及摩擦学性能的影响
|
|
毕健浩男, 张艳, 王振玉, 周晟昊, 刘永跃, 张小岩, 汪爱英
|
Effect of Mo Content on the Microstructure, Mechanical and Tribological Properties of CrAlMoN Coatings
|
|
BI Jianhaonan, ZHANG Yan, WANG Zhenyu, ZHOU Shenghao, LIU Yongyue, ZHANG Xiaoyan, WANG Aiying
|
|
表2 不同位置CrAlMoN涂层的化学组成、厚度和表面粗糙度
|
Table 2 Chemical compositions, thicknesses, and surface roughnesses of CrAlMoN coatings at different positions
|
|
| Sample | Atomic fraction / % | Thickness μm | Roughness μm |
|---|
| Cr | Al | Mo | N |
|---|
| A1 | 22.28 ± 0.01 | 36.76 ± 0.25 | 0.72 ± 0.02 | 37.48 ± 0.24 | 9.32 | 0.150 ± 0.044 | | A2 | 22.74 ± 0.12 | 36.18 ± 0.22 | 1.21 ± 0.03 | 37.39 ± 0.22 | 7.15 | 0.219 ± 0.010 | | A3 | 23.42 ± 0.25 | 34.15 ± 0.32 | 2.55 ± 0.03 | 36.71 ± 0.30 | 6.35 | 0.137 ± 0.024 | | A4 | 26.89 ± 0.28 | 27.53 ± 0.16 | 6.38 ± 0.22 | 33.90 ± 0.17 | 6.01 | 0.080 ± 0.029 | | C1 | 38.40 ± 0.57 | 8.64 ± 0.09 | 16.50 ± 0.31 | 25.14 ± 0.41 | 6.16 | 0.200 ± 0.043 | | C2 | 44.73 ± 0.84 | 1.04 ± 0.04 | 19.47 ± 0.34 | 20.51 ± 0.34 | 8.86 | 0.082 ± 0.005 |
|
|
|