聚变用低活化9Cr-ODS钢在高温高压水中的腐蚀行为及机理
Corrosion Behavior and Mechanism of Low Activation 9Cr-ODS Steel in High Temperature and High Pressure Water Environment for the Application in Fusion Reactors
聚变用低活化9Cr-ODS钢在高温高压水中的腐蚀行为及机理 |
| 付海阳, 张家榕, 李尧志, 王旗涛, 李新乐, 严伟, 单以银, 李艳芬 |
|
Corrosion Behavior and Mechanism of Low Activation 9Cr-ODS Steel in High Temperature and High Pressure Water Environment for the Application in Fusion Reactors |
| FU Haiyang, ZHANG Jiarong, LI Yaozhi, WANG Qitao, LI Xinle, YAN Wei, SHAN Yiyin, LI Yanfen |
| 图13 9Cr-ODS钢在动态高温高压水中腐蚀1000 h后氧化膜截面的TEM像和SAED花样 |
| Fig.13 Cross-sectional TEM image (a) of oxide film of 9Cr-ODS steel after corrosion in dynamic high temperature and high pressure water for 1000 h, and corresponding SAED patterns of zone A (b) and zone B (c) in Fig.13a |
|
|