锆合金氧化膜中相变与裂纹演化的相场模拟
Phase-Field Simulations of Phase Transformation and Crack Evolution in Zirconium Alloy Oxide Film
(a1-a4) principal stress S11 (b1-b4) principal stress S22 (c1-c4) shear stress S12
锆合金氧化膜中相变与裂纹演化的相场模拟 |
| 王小齐, 张金虎, 郭辉, 李学雄, 许海生, 柏春光, 徐东生, 杨锐 |
|
Phase-Field Simulations of Phase Transformation and Crack Evolution in Zirconium Alloy Oxide Film |
| WANG Xiaoqi, ZHANG Jinhu, GUO Hui, LI Xuexiong, XU Haisheng, BAI Chunguang, XU Dongsheng, YANG Rui |
| 图3 m-ZrO2晶粒长大过程中的应力分布演化 |
| Fig.3 Evolution of stress distribution during the growth of m-ZrO2 at t = 1.0 × 10-12 s (a1-c1), t = 6.0 × 10-8 s (a2-c2), t = 1.0 × 10-7 s (a3-c3), and t = 3.0 × 10-7 s (a4-c4) (a1-a4) principal stress S11 (b1-b4) principal stress S22 (c1-c4) shear stress S12 |
|
|