含<strong>Cr</strong>耐蚀钢筋在模拟高碱性混凝土孔隙液中的钝化行为

含Cr耐蚀钢筋在模拟高碱性混凝土孔隙液中的钝化行为

王慕亮, 孙玉朋, 陈磊, 魏洁, 董俊华

Passive Behavior of Corrosion-Resistant Cr-Containing Steel Bars in Simulated High-Alkaline Concrete Pore Solution

WANG Muliang, SUN Yupeng, CHEN Lei, WEI Jie, DONG Junhua

表3 20MnSi、3Cr和9Cr钢在模拟混凝土溶液中浸泡不同时间后点缺陷密度 (10²¹ cm^-3)

Table 3 Point defect densities of 20MnSi, 3Cr, and 9Cr steels in simulated concrete pore solution after different immersion time

Time h	20MnSi		3Cr		9Cr
Time h	R1	R2	R1	R2	R1	R2
0.5	4.88	5.20	3.62	5.18	3.57	3.48
12	4.52	5.06	3.46	3.89	2.45	3.04
24	4.11	4.42	3.13	3.48	2.32	2.94
72	3.39	3.90	2.92	3.29	1.94	2.57
168	2.54	3.25	2.16	2.48	1.81	2.27