利用热轧制-剪切-弯曲工艺及退火调控Mg-Al-Zn-Mn-Ca 镁合金的织构
Controlling the Texture of Mg-Al-Zn-Mn-Ca Magnesium Alloy by Hot Rolling-Shearing-Bending Process and Annealing
(a, e) 0°-20° group (b, f) 45°-70° group (c, g) 20°-45° group (d, h) 70°-90° group
利用热轧制-剪切-弯曲工艺及退火调控Mg-Al-Zn-Mn-Ca 镁合金的织构 |
| 游云翔, 谭力, 高静静, 周涛, 周志明 |
|
Controlling the Texture of Mg-Al-Zn-Mn-Ca Magnesium Alloy by Hot Rolling-Shearing-Bending Process and Annealing |
| YOU Yunxiang, TAN Li, GAO Jingjing, ZHOU Tao, ZHOU Zhiming |
| 图12 不同退火温度后非基面织构Mg-2Al-2Zn-0.4Mn-0.5Ca镁合金板材的织构组分分布 |
| Fig.12 Texture component distributions of non-basal textured Mg-2Al-2Zn-0.4Mn-0.5Ca magnesium alloy sheets annealed at 400 oC (a-d) and 450 oC (e-h) for 1 h (Insets are corresponding (0002) pole figures) (a, e) 0°-20° group (b, f) 45°-70° group (c, g) 20°-45° group (d, h) 70°-90° group |
|
|