利用热轧制-剪切-弯曲工艺及退火调控Mg-Al-Zn-Mn-Ca 镁合金的织构
游云翔, 谭力, 高静静, 周涛, 周志明

Controlling the Texture of Mg-Al-Zn-Mn-Ca Magnesium Alloy by Hot Rolling-Shearing-Bending Process and Annealing
YOU Yunxiang, TAN Li, GAO Jingjing, ZHOU Tao, ZHOU Zhiming
图5 HRSB处理及400 ℃退火1 h后,非基面织构Mg-2Al-2Zn-0.4Mn-0.5Ca镁合金板材沿不同方向拉伸后的室温真应力-应变曲线
Fig.5 Room temperature true stress-strain curves after tensile tests along RD and TD for Mg-2Al-2Zn-0.4Mn-0.5Ca magnesium alloy sheets with non-basal texture after HRSB treatment and annealing at 400 oC for 1 h