利用热轧制-剪切-弯曲工艺及退火调控Mg-Al-Zn-Mn-Ca 镁合金的织构 |
游云翔, 谭力, 高静静, 周涛, 周志明 |
Controlling the Texture of Mg-Al-Zn-Mn-Ca Magnesium Alloy by Hot Rolling-Shearing-Bending Process and Annealing |
YOU Yunxiang, TAN Li, GAO Jingjing, ZHOU Tao, ZHOU Zhiming |
图2 热轧制及退火态Mg-2Al-2Zn-0.4Mn-0.5Ca镁合金板材的织构演化 |
Fig.2 Texture evolutions of hot-rolled (a) and as-annealed (b-d) Mg-2Al-2Zn-0.4Mn-0.5Ca magnesium alloy sheets (RD—rolling direction, TD—transverse direction) (b) 350 oC for 1 h (c) 400 oC for 1 h (d) 450 oC for 1 h |
![]() |