一种镍基高温合金的高温HCl腐蚀行为
High-Temperature Corrosion Behavior of a Nickel-Based Superalloy in HCl-Containing Atmosphere
一种镍基高温合金的高温HCl腐蚀行为 |
| 周一鸣, 韩勇军, 谢光, 郑伟, 肖炎彬, 潘阳, 张健 |
|
High-Temperature Corrosion Behavior of a Nickel-Based Superalloy in HCl-Containing Atmosphere |
| ZHOU Yiming, HAN Yongjun, XIE Guang, ZHENG Wei, XIAO Yanbin, PAN Yang, ZHANG Jian |
| 图11 镍基高温合金腐蚀不同时间后截面沿晶界内氧化形貌的SEM-BSE像 |
| Fig.11 Cross sectional SEM-BSE images showing the internal oxidation morphologies along grain boundaries for nickel-based superalloy after corroded for 75 h (a), 100 h (b), and 200 h (c) |
|
|