先进镍基粉末高温合金FGH4108在不同应力条件下的蠕变行为
|
李新宇, 白佳铭, 张浩鹏, 李晓鲲, 贾建, 刘常升, 刘建涛, 张义文
|
Creep Behavior of Advanced Powder Metallurgy Nickel-Based Superalloys FGH4108 Under Different Stress Conditions
|
LI Xinyu, BAI Jiaming, ZHANG Haopeng, LI Xiaokun, JIA Jian, LIU Changsheng, LIU Jiantao, ZHANG Yiwen
|
|
表2 在700 ℃下粗晶和细晶FGH4108合金的最小蠕变速率和各蠕变阶段的应变和时间
|
Table 2 Minimum creep rates (˙εm) and strains and time of creep stages of the coarse grain and fine grain samples at 700 oC
|
|
Sample | Stress MPa | ˙εm s-1 | First stage | Second stage | Third stage |
---|
ε1 % | ε1 / ε % | t1 h | t1 / tr % | ε2 % | ε2 / ε % | t2 h | t2 / tr % | ε3 % | ε3 / ε % | t3 h | t3 / tr % |
---|
Coarse grain | 900 | 1.02 × 10-7 | 0.7 | 29.1 | 14.2 | 23.2 | 1.7 | 70.8 | 47.0 | 76.8 | - | - | - | - | | 810 | 2.19 × 10-8 | 0.3 | 12.5 | 17.0 | 6.8 | 2.1 | 87.5 | 233.0 | 93.2 | - | - | - | - | | 780 | 8.15 × 10-9 | 0.5 | 10.2 | 145.5 | 14.8 | 0.6 | 12.2 | 166.3 | 16.9 | 3.8 | 77.6 | 670.2 | 68.2 | Fine grain | 900 | 7.77 × 10-7 | 1.1 | 23.4 | 3.8 | 27.1 | 0.7 | 14.9 | 2.4 | 17.1 | 2.9 | 61.7 | 7.8 | 55.7 | | 810 | 9.53 × 10-8 | 0.6 | 6.9 | 15.6 | 14.9 | 0.9 | 10.3 | 18.9 | 18.0 | 7.2 | 82.8 | 70.5 | 67.1 | | 780 | 7.61 × 10-8 | 0.4 | 9.3 | 11.6 | 13.4 | 0.4 | 9.3 | 13.7 | 15.8 | 3.5 | 81.4 | 61.5 | 70.8 |
|
|
|