机械合金化AlCrCu0.5Mo0.5Ni高熵合金及其后续退火态的结构演化
Microstructure Evolution of Mechanically-Alloying and Its Subsequently-Annealed AlCrCu0.5Mo0.5Ni High-Entropy Alloy
机械合金化AlCrCu0.5Mo0.5Ni高熵合金及其后续退火态的结构演化 |
| 雷云龙, 杨康, 辛越, 姜自滔, 童宝宏, 张世宏 |
|
Microstructure Evolution of Mechanically-Alloying and Its Subsequently-Annealed AlCrCu0.5Mo0.5Ni High-Entropy Alloy |
| LEI Yunlong, YANG Kang, XIN Yue, JIANG Zitao, TONG Baohong, ZHANG Shihong |
| 图11 1200 ℃退火后MA 40 h粉末的TEM明场像、选区电子衍射(SAED)花样和EDS元素分布图 |
| Fig.11 Bright-field TEM image (a), selected area electron diffraction (SAED) patterns of the areas B (b) and C (c) in Fig.11a, and dark-field TEM image and EDS elemental distributions (d) of MA 40 h powders after annealing at 1200 oC |
|
|