机械合金化AlCrCu0.5Mo0.5Ni高熵合金及其后续退火态的结构演化
Microstructure Evolution of Mechanically-Alloying and Its Subsequently-Annealed AlCrCu0.5Mo0.5Ni High-Entropy Alloy
(a) 10 h (b) 20 h (c) 40 h (d) 60 h
机械合金化AlCrCu0.5Mo0.5Ni高熵合金及其后续退火态的结构演化 |
| 雷云龙, 杨康, 辛越, 姜自滔, 童宝宏, 张世宏 |
|
Microstructure Evolution of Mechanically-Alloying and Its Subsequently-Annealed AlCrCu0.5Mo0.5Ni High-Entropy Alloy |
| LEI Yunlong, YANG Kang, XIN Yue, JIANG Zitao, TONG Baohong, ZHANG Shihong |
| 图5 不同球磨时间下MA粉末的表面形貌 |
| Fig.5 Surface morphologies of MA powder after different ball milling time (a) 10 h (b) 20 h (c) 40 h (d) 60 h |
|
|