马氏体-奥氏体组元特征分布对复相钢扩孔行为的影响 |
杨晓宇, 米振莉, 方幸, 刘航瑞, 牟望重 |
Achieving an Excellent Hole Expansion Behavior in Complex Phase Steels by Characteristic Distribution of Martensite-Austenite Constituents |
YANG Xiaoyu, MI Zhenli, FANG Xing, LIU Hangrui, MU Wangzhong |
图8 基准钢和实验用钢在扩孔变形过程中从初始、损伤至失效示意图 |
Fig.8 Schematics of base steel (a-c) and advanced steel (d-f) in original state (a, d), damage (b, e), and failure (c, f) during hole expansion deformation |
![]() |