Ag替换Cu对Zr-Ti-Cu-Al非晶合金性能的影响
|
|
蔡正清, 尹大伟, 杨靓, 王文祥, 王飞龙, 温永清, 马明臻
|
Effect of Ag Substitution of Cu on Properties of Zr-Ti-Cu-Al Amorphous Alloys
|
|
CAI Zhengqing, YIN Dawei, YANG Liang, WANG Wenxiang, WANG Feilong, WEN Yongqing, MA Mingzhen
|
|
表2 Zr55Ti3Cu32 - x Al10Ag x 非晶合金在不同加热速率下的特征温度
|
Table 2 Characteristic temperatures of Zr55Ti3Cu32 - x Al10-Ag x BMGsat different heating rates (β)
|
|
| x | β / (K·min-1) | Tg / K | Tx / K | Tp1 / K | Tp2 / K |
|---|
| 0 | 10 | 665.2 | 721.9 | 724.2 | 854.3 | | 20 | 673.0 | 730.4 | 732.9 | 872.4 | | 30 | 674.7 | 736.6 | 739.3 | 886.6 | | 40 | 681.7 | 740.1 | 742.9 | 895.5 | | 1 | 10 | 665.2 | 720.7 | 723.1 | 868.6 | | 20 | 667.2 | 729.7 | 731.5 | 890.1 | | 30 | 676.3 | 734.6 | 736.9 | 900.8 | | 40 | 680.5 | 738.3 | 741.0 | 909.9 | | 1.5 | 10 | 661.3 | 718 | 721.3 | 879.4 | | 20 | 673.8 | 727.2 | 729.9 | 899.9 | | 30 | 674.0 | 733.3 | 735.8 | 911.8 | | 40 | 674.6 | 735.4 | 738.6 | 918.2 | | 2 | 10 | 662.2 | 718 | 721.2 | 886.1 | | 20 | 665.1 | 726.4 | 729.8 | 904.5 | | 30 | 673.7 | 732.1 | 735.2 | 914.3 | | 40 | 674.5 | 736.5 | 739.8 | 923.2 | | 2.5 | 10 | 663.1 | 718.2 | 721.7 | 888.8 | | 20 | 665.0 | 727.1 | 730.0 | 904.9 | | 30 | 671.5 | 731.8 | 735.4 | 915.0 | | 40 | 672.0 | 735.9 | 738.8 | 921.8 |
|
|
|