AZ31镁合金双峰组织形成机制及其变形行为
Formation Mechanism and Deformation Behavior of AZ31 Magnesium Alloy Bimodal Structure
(a) //ED (b) ⊥ED
AZ31镁合金双峰组织形成机制及其变形行为 |
| 周雯慧, 熊锦涛, 黄思程, 王鹏昊, 刘勇 |
|
Formation Mechanism and Deformation Behavior of AZ31 Magnesium Alloy Bimodal Structure |
| ZHOU Wenhui, XIONG Jintao, HUANG Sicheng, WANG Penghao, LIU Yong |
| 图3 不同方向双峰组织AZ31镁合金的典型OM像 |
| Fig.3 Typical OM images of bimodal structure AZ31 magnesium alloy (Blue circle is fine equiaxed grains (FEGs), yellow circle is row stacked grains (RSGs), and red circle is long elongated grains (LEGs); DRX—dynamic recrystallization) (a) //ED (b) ⊥ED |
|
|