聚变增殖包层用低活化9Cr-ODS钢的室温低周疲劳行为
王旗涛, 李艳芬, 张家榕, 李尧志, 付海阳, 李新乐, 严伟, 单以银

Low Cycle Fatigue Behavior of 9Cr-ODS Steel as a Fusion Blanket Structural Material at Room Temperature
WANG Qitao, LI Yanfen, ZHANG Jiarong, LI Yaozhi, FU Haiyang, LI Xinle, YAN Wei, SHAN Yiyin
图8 9Cr-ODS钢在热处理态和不同应变幅下的晶粒平均取向差(GAM)图
Fig.8 Grain average misorientation (GAM) maps of 9Cr-ODS steel after normalizing & tempering treatment (a) and under Δεt / 2 = 0.3% (b), Δεt / 2 = 0.5% (c), and Δεt / 2 = 0.8% (d)