静水压力和拉伸应力交互作用下Ni-Cr-Mo-V钢在3.5%NaCl溶液中的应力腐蚀行为
Stress Corrosion Behavior of Ni-Cr-Mo-V Steel in 3.5%NaCl Solution Under the Interaction of Hydrostatic Pressure and Tensile Stress
(a, b) 1 × 10-6 s-1 (c, d) 5 × 10-6 s-1
静水压力和拉伸应力交互作用下Ni-Cr-Mo-V钢在3.5%NaCl溶液中的应力腐蚀行为 |
| 宋昱杉, 刘叡, 崔宇, 刘莉, 王福会 |
|
Stress Corrosion Behavior of Ni-Cr-Mo-V Steel in 3.5%NaCl Solution Under the Interaction of Hydrostatic Pressure and Tensile Stress |
| SONG Yushan, LIU Rui, CUI Yu, LIU Li, WANG Fuhui |
| 图7 Ni-Cr-Mo-V钢在不同环境中经过SSRT实验后的断口纤维区裂纹 |
| Fig.7 Magnified cracks on the fibrous zone of Ni-Cr-Mo-V steel fracture after SSRT test at 0.1 MPa (a, c) and 20 MPa (b, d) in 3.5%NaCl solution (a, b) 1 × 10-6 s-1 (c, d) 5 × 10-6 s-1 |
|
|